Template-based growth of titanium dioxide nanorods by a particulate sol-electrophoretic deposition process

Particuology 2011年第2期9卷 161-169页

作者： Mohammad Reza Mohammadi Farideh Ordikhani Derek J.Fray farzad khomamizadeh Department of Materials Science & Engineering Sharif University of Technology Department of Materials Science & Metallurgy University of Cambridge

TiO2 nanorods have been successfully grown into a track-etched polycarbonate （PC） membrane by a particulate sol-electrophoretic deposition from an aqueous medium. The prepared sols had a narrow particle size distribution around 17 nm and excellent stability against aging, with zeta potentials in the range of 47-50 mV at pH 2. It was found that TiO2 nanorods were grown from dilute aqueous sol with a low, 0.1-M concentration. Fourier transform infrared spectroscopy （FT-IR） analysis confirmed that a full conversion of titanium isopropoxide was obtained by hydrolysis, resulting in the formation of TiO2 particles. X-ray diffraction （XRD） results revealed that TiO2 nanorods dried at 100℃ were a mixture of anatase and brookite phases, whereas they were a mixture of anatase and futile structures at 500℃. Moreover, the rutile content of the TiO2 nanorods was higher than that of TiO2 powders. Transmission electron microscope （TEM） images confirmed that TiO2 nanorods had a smooth morphology and longi- tudinal uniformity in diameter. Field emission scanning electron microscope （FE-SEM） images showed that TiO2 nanorods grown by sol-electrophoresis from the dilute aqueous sol had a dense structure with a uniform diameter of 200 rim, containing small particles with an average size of 15 nm. Simultaneous differential thermal （SDT） analysis verified that individual TiO2 nanorods, grown into a PC template, were obtained after annealing at 500℃. Based on kinetic studies, it was found that uniform TiO2 nanorods with high-quality morphology were obtained under optimum conditions at an applied potential of 0.3 V/cm and a deposition time of 60 min.

关键词： Nanorod Crystal morphology Electrophoretic deposition Sol-electrophoresisTitanium dioxide

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：