Carbonation of low heat portland cement paste precured in water for different time

Journal of University of Science and Technology Beijing 2007年第2期14卷 178-184页

作者： Deping Chen etsuo sakai Masaki Daimon Yoko Ohba Civil and Environmental Engineering School University of Science and Technology Beijing Beijing 100083 China Graduate School of Science and Engineering Tokyo Institute of Technology Tokyo 152-8552 Japan

The carbonation technique was applied to accelerate the hydration of low heat portland cement （LHC）. Before carbonation, the demoulded pastes were precured in water for 0, 2, 7, and 21 d, respectively. The results show that precuring time in water strongly influences the carbonation process. The phenolphthalein test indicates that the paste precured in water for a shorter time is more quickly carbonated than that for a longer time. The content of calcium hydroxide increases with increasing the precuring time in water, whereas, the amount of absorbed carbon dioxide changes contrarily. Scanning electron microscope （SEM） observation shows that portlandite always fills up big air bubbles in the paste during precuring in water, and the mercury intrusion porosimetry （MIP） results show that there are less large capillary pores in the paste precured in water for a longer time. It is found that the paste without precuring in water has more carbon dioxide absorption during curing in carbon dioxide atmosphere, and its total pore volume decreases remarkably with an increase in the carbonation time than that precured in water. X-ray diffraction （XRD） and Brunauer-Emmett-Teller （BET） surface area analyses indicate that the carbonate products are vaterite and calcite; CxSHy formed from carbonation has low BET surface area in comparison with that of C-S-H formed from curing in water.

关键词： carbonation carbon dioxide absorption vaterite BET surface area pore size distribution

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

DISPERSION MECHANISMS OF COMB-TYPE SUPERPLASTICIZERS CONTAINING GRAFTED POLYETHYLENE OXIDES

DISPERSION MECHANISMS OF COMB-TYPE SUPERPLASTICIZERS CONTAIN...

引用

第五届水泥与混凝土国际会议

作者： sakai etsuo DAIMON Masaki Tokyo Institute of Technology 2-12-1 OokayamaMeguro-kuTokyoJAPAN152-8552

This paper discusses on graft chain length of comb-type superplasticizers affecting the adsorption and dispersion mechanisms, and their subsequent effect on the fluidity of limestone powder suspensions. Contrary to the results obtained from interparticle potential calculations, the fluidity of concentrated suspension is improved by the use of comb-type polymers having shorter grafted chain length. The dispersion mechanism of comb-type polymers in a concentrated suspension is evaluated from the perspective of molecular structure, the amount of adsorbed polymer, and the amount of entrapped water in the clusters of CaCO3 particles. Furthermore, the addition of certain soluble salts, which can effect the concentration of Ca2+ in liquid phase of CaCO3 suspensions, has been observed to decrease the adsorption of comb-type polymers on CaCO3. Thus, the polymer adsorption process can be selectively influenced by certain types of ions

关键词： comb-type superplasticezer grafted chain dispersion mechanisms steric hindrance

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

CONTROL METHODS FOR THE EARLY HYDARTION IN Ca3Al2O6--GYPSUM SYSTEM WITH SUPERPLASTICIZERS

CONTROL METHODS FOR THE EARLY HYDARTION IN Ca3Al2O6--GYPSUM ...

引用

第五届水泥与混凝土国际会议

作者： sakai etsuo Kang Jin-Kyu Daimon Masaki Tokyo Institute of Technology 2-12-1 OokayamaMeguro-kuTokyoJAPAN152-8552

It is necessary to control the early hydration of aluminate phase in order to control the fluidity. The object of this paper is to obtain the basic data for the fluidity control of cement and concrete with superplasticizers. This paper discusses the influence of superplasticizers on the early hydration of C3A-calcium sulfates by quantitative XRD. And the control methods of the hydration in C3A-gypsum system with supperplasticizers have been proposed. The early hydration of C3A is retarded, as there is much content of SO42- in the gel formed around C3 A. Adding of comb-type superplasticizers in C3A-calcium sulfates systems accelerates early hydration of C3 A, because the supply of SO42- to gel is inhibited. The early hydration of C3A in C3 A-gypsum system is retarded by replacement of gypsum to hemihydrate or increasing free-CaO contents. It is proposed that the replacement of about 50% of gypsum to hemihydrate or the increase of CaO contenets would be effective for controlling the early hydration of cement with comb-type superplasticizers.

关键词： wuperplasticizers early hydration C3A calcium sulfates free-CaO

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

日本化学外加剂发展的新趋势(下)

引用

商品混凝土 2007年第3期 62-66页

作者： etsuo sakai Atsumu Ishida Akira Ohta 罗小红

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

日本化学外加剂发展的新趋势(上)

引用

商品混凝土 2007年第2期 73-77页

作者： etsuo sakai Atsumu Ishida Akira Ohta 罗小红

本文主要介绍了日本化学外加剂发展历史及其最新的发展趋势。聚羧酸系减水剂是目前日本超塑化剂市场上的主要产品。而最近他们又在传统聚羧酸系超塑化剂研究的基础上,开发出了一种新型的低粘度型聚羧酸系超塑化剂。掺有这种低粘度聚羧... 详细信息

本文主要介绍了日本化学外加剂发展历史及其最新的发展趋势。聚羧酸系减水剂是目前日本超塑化剂市场上的主要产品。而最近他们又在传统聚羧酸系超塑化剂研究的基础上,开发出了一种新型的低粘度型聚羧酸系超塑化剂。掺有这种低粘度聚羧酸系超塑化剂的混凝土的流动速度比掺有传统聚羧酸系超塑化剂的混凝土的流动速度快。而加入一种同时含有阴离子和阳离子表面活性剂的新型增稠剂后,在新拌混凝土中会形成三维网状结构,水泥浆体的粘度增加并且可以避免离析。通过加入缓凝剂可以控制浆体中水泥的水化,因为在水泥浆中存在着许多的未反应的阿利特相,所以水泥的比表面积并没有增加。当在水泥浆中加入缓凝剂葡萄糖酸钠时,不会对混凝土的性能产生不利的影响,因此有利于搅拌站延长混凝土的浇注时间。目前在喷射混凝土工艺中,液体和粉状铝酸钙系(CA)速凝剂以及硫铝酸钙系(CSA)速凝剂已经得到了广泛的应用。对于CA速凝剂而言,随着其加入量的增加砂浆的终凝时间会加快,而在掺有CSA速凝剂的砂浆中,随着其加入量的增加砂浆的初凝时间和终凝时间均会缩短。

关键词：聚羧酸系超塑化剂化学外加剂水泥浆体新拌混凝土缓凝剂硫铝酸钙葡萄糖酸钠终凝时间减缩剂

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

5%乙烯-醋酸乙烯共聚物复合低热水泥浆体的碳化促进养护

引用

硅酸盐学报 2006年第10期34卷 1263-1269页

作者：陈德平坂井悦郎大场阳子大门正机北京科技大学土木工程系北京100083 东京工业大学大学院理工学研究科

采用碳化养护方法促进5%乙烯-醋酸乙烯共聚物复合低热水泥浆体的水化。通过X射线衍射定性及定量分析测定了养护后样品的组成及水泥中硅酸三钙(3CaO·SiO2,C3S)、硅酸二钙(2CaO·SiO2,C2S)的水化率;利用带固体样品测试装置的全有机碳素... 详细信息

采用碳化养护方法促进5%乙烯-醋酸乙烯共聚物复合低热水泥浆体的水化。通过X射线衍射定性及定量分析测定了养护后样品的组成及水泥中硅酸三钙(3CaO·SiO2,C3S)、硅酸二钙(2CaO·SiO2,C2S)的水化率;利用带固体样品测试装置的全有机碳素分析仪测定了样品所吸收的CO2量;采用水银压入法检测了样品的孔径分布。结果显示:碳化养护大大促进了低热水泥的水化,并有球霰石生成。样品中的总孔隙体积也明显减少,但有大量较大孔径的毛细孔隙存在。碳化养护前,对样品进行水中预养护可以减少这些毛细孔隙,但不利于水泥的水化并导致CO2吸收量及抗折强度显著降低。

关键词：碳化乙烯-醋酸乙烯共聚物低热水泥球霰石二氧化碳吸收孔径分布

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

日本化学外加剂发展的新趋势

日本化学外加剂发展的新趋势

引用

2008中国商品混凝土可持续发展论坛暨第五届全国商品混凝土技术交流大会

作者： etsuo sakai Atsumu Ishida Akira Ohta 罗小红

本文主要介绍了日本化学外加剂发展历史及其最新的发展趋势。聚羧酸系减水剂是目前日本超塑化剂市场上的主要产品。而最近他们又在传统聚羧酸系超塑化剂研究的基础上,开发出了一种新型的低粘度型聚羧酸系超塑化剂。掺有这种低粘度聚羧酸系超塑化剂的混凝土的流动速度比掺有传统聚羧酸系超塑化剂的混凝土的流动速度快。而加入一种同时含有阴离子和阳离子表面活性剂的新型增稠剂后,在新拌混凝土中会形成三维网状结构,水泥浆体的粘度增加并且可以避免离析。通过加入缓凝剂可以控制浆体中水泥的水化,因为在水泥浆中存在着许多的未反应的阿利特相,所以水泥的比表面积并没有增加。当在水泥浆中加入缓凝剂葡萄糖酸钠时,不会对混凝土的性能产生不利的影响,冈此有利于搅拌站延长混凝土的浇注时间。目前在喷射混凝土工艺中,液体和粉状铝酸钙系(CA)速凝剂以及硫铝酸钙系(CSA)速凝剂已经得到了广泛的应用。对于CA速凝剂而言,随着其加入量的增加砂浆的终凝时间会加快,而在掺有CSA速凝剂的砂浆中,随着其加入量的增加砂浆的初凝时间和终凝时间均会缩短。

关键词：建设材料混凝土外加剂流动速度比

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：