Failure Analysis of the Semi-permanent Coupler Used in Metro Rail

Failure Analysis of the Semi-permanent Coupler Used in Metro...

作者： M A Morsy S Khafagy es mosa Welding and NDT Dept. CMRDI TIMS Al-Azhar University Faculty of Engineering Mining and Petroleum Engineering Dept.

Failure analysis of the semi-permanent coupler which failed in service of Metro rail was conducted in order to know the reason for failure. The examinations include visual, photo detection, chemical analysis, hardness measurements, tensile and v-notch impact test, microstructure and SEM observation of fracture surface. Chemical analysis and tensile test shows that the coupler material can be classified as grade B cast steel in AAR M201 steel casting specification. Although the microstructure of the coupler material shows incomplete homogenization indicating the improper conduction of heat treatment, the v-notch impact results is accepted according to this specification. The fracture surface shows the existence of much porosity at the internal surface of the hollow like pipe-coupler and the fracture started at these sites showing beach marks. SEM observation of the fracture surface shows fatigue striations indicating the occurrence of fatigue started at the porosity defects. The cast defects act as a stress concentration site for fatigue crack initiation. Crack occurred, propagated, and connected the defects to each other. The occurrence of collision resulted in bending of the female part of the coupler（plastic deformation occurs） at the lower thin wall（～ 5.41 mm thickness）. Moreover, opening of the previously formed fatigue crack and accelerating the failure were occurred. Recommendations were explained to prevent the occurrence of this failure.

关键词： failure analysis coupler chemical analysis mechanical testing microstructure fracture surface fatigue porosity crack

来源： cnki会议评论

在线全文

cnki会议

学校读者我要写书评

暂无评论

全选清除本页清除全部题录导出标记到“检索档案”

共1页 << < 1 > >>

回到顶部

执行限定条件

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：