Gas sensing capabilities of TiO_(2) porous nanoceramics prepared through premature sintering

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Journal of Advanced Ceramics 2015年第2期4卷 152-157页

作者： Yao XIONG Zilong TANG Yu waNG Yongming HU Haoshuang GU Yuanzhi LI helen lai wah chan wanping CHEN Key Laboratory of Artificial Micro-and Nano-structures of Ministry of Education and School of Physics and Technology Wuhan UniversityWuhan 430072China School of Materials Science and Engineering State Key Laboratory of New Ceramics and Fine ProcessingTsinghua UniversityBeijing 100084China Department of Applied Physics and Materials Research Centre The Hong Kong Polytechnic UniversityHong KongChina Faculty of Physics and Electronic Technology Hubei UniversityWuhan 430062China State Key Laboratory of Silicate Materials for Architectures Wuhan University of TechnologyWuhan 430070China

Pure and noble metal(Pt,Pd,and Au)doped TiO_(2)nanoceramics have been prepared from TiO_(2)nanoparticles through traditional pressing and *** those samples sintered at 550℃,a typical premature sintering occurred,which led to the formation of a highly porous microstructure with a Brunauer-Emmett-Teller(BET)specific surface area of 23 m^(2)/*** room temperature,only Pt-doped samples showed obvious response to hydrogen,with sensitivities as high as~500 for 1000 ppm H_(2)in N_(2);at 300℃,all samples showed obvious responses to CO,while the responses of noble metal doped samples were much higher than that of the undoped *** mechanism for the observed sensing capabilities has been discussed,in which the catalytic effect of Pt for hydrogen is believed responsible for the room-temperature hydrogen sensing capabilities,and the absence of glass frit as commonly used in commercial thick-film metal oxide gas sensors is related to the high *** is proposed that much attention should be paid to metal oxide porous nanoceramics in developing gas sensors with high sensitivities and low working temperatures.

关键词： TiO_(2) porous nanoceramics premature sintering sensors hydrogen CO

锌铌酸铅-锆钛酸铅(PZN-PZT)压电陶瓷和陶瓷纤维的制备

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

无机材料学报 2005年第5期20卷 1099-1105页

作者：李坤曹大呼李金华陈王丽华江苏工业学院材料系信息科学系常州213016 香港理工大学应用物理系

以乙酸铅、丙酸锌、五乙氧基铌、四丙氧基锆和四正丁氧基钛为原料,用溶胶-凝胶法制备了锌铌酸铅-锆钛酸铅(PZN-PZT)凝胶纤维.该纤维经热解、烧结后成为直径约25μm的陶瓷纤维.陶瓷纤维的表面和断面形貌的电子扫描图像显示:该陶瓷纤维均... 详细信息

以乙酸铅、丙酸锌、五乙氧基铌、四丙氧基锆和四正丁氧基钛为原料,用溶胶-凝胶法制备了锌铌酸铅-锆钛酸铅(PZN-PZT)凝胶纤维.该纤维经热解、烧结后成为直径约25μm的陶瓷纤维.陶瓷纤维的表面和断面形貌的电子扫描图像显示:该陶瓷纤维均匀致密,呈圆柱形.X射线分析表明:烧结温度影响陶瓷的晶相纯度.当烧结温度高于1250℃时,该陶瓷及陶瓷纤维呈现纯净的钙钛矿晶相.阿基米德法测得陶瓷和陶瓷纤维的密度分别为7.70×103kg/m3和7.80×103kg/m3.对陶瓷含量为63%的PZN-PZT陶瓷纤维/环氧树脂1-3复合材料压电片,测得其机电转换常数kt、压电常数d33和相对介电常数ε分别为:0.65、403pC/N和1300.以溶胶-凝胶法制备的超细粉体为原料烧结成的PZN-PZT陶瓷,其kt、d33和ε分别为0.48、600pC/N和2627.

关键词：陶瓷纤维 1-3复合材料溶胶-凝胶法锆钛酸铅

A ＂tricky＂ subarachnoid hemorrhage

在线全文

学校读者我要写书评

暂无评论

Chinese Medical Journal 2013年第18期126卷 3598-3598页

作者： SHEA Yat-fung TSANG Hoi-lun helen YAP Yat-hin Desmond LI lai-fung HO wai-shing Wilson Department of Medicine Queen Mary tlospital The University of Hong Kong Hong Kong China Division of Neurosurgery Department of Surgery Queen Mary tlospital The University of Hong Kong Hong Kong China

To the editor： We report a tricky subarachnoid haemorrhage （SAH）. Our patient was a 59-year-old woman with generalizedheadache for 1 day, which was constricting in nature and rated grade 6/10. Her symptoms were aggravated by lying flat and improved with vomiting. The Glasgow coma scale was lull, blood pressure was 142/83 mmHg and pulse 75 beats/min. There was neither neck stiffness nor focal neurological deficit. Fundoscopic examination was normal. She was noted to have hyponatremia （sodium （Na） 122 mmol/L） with serum osmolarity 263 mmol/kg, urine osmolarity 582 mmol/kg, urine Na I 17 retool/L, nomaal thyroid stimulating hormone and cortisol level.

关键词： RED-BLOOD-CELLS LUMBAR PUNCTURE ANEURYSMS CT

YBa_2Cu_3O_(7-x)纳米单晶超导性和室温铁磁性研究

在线全文

学校读者我要写书评

暂无评论

陶瓷学报 2014年第6期35卷 573-576页

作者：沈振江邴丽娜陈万平王雨陈王丽华江向平海南师范大学物理与电子工程学院海南海口571158 香港理工大学应用物理系景德镇陶瓷学院材料科学与工程学院江西景德镇333403

采用软化学法制备了YBa2Cu3O7-x(YBCO)纳米单晶,并与利用传统固相法制备出YBCO陶瓷粉末作对比。性能测试表明:YBCO纳米单晶的晶体结构为具有高结晶度和良好单相性的正交对称钙钛矿结构,其具有200 nm-500 nm的粒度尺寸和很好的单晶结构,... 详细信息

采用软化学法制备了YBa2Cu3O7-x(YBCO)纳米单晶,并与利用传统固相法制备出YBCO陶瓷粉末作对比。性能测试表明:YBCO纳米单晶的晶体结构为具有高结晶度和良好单相性的正交对称钙钛矿结构,其具有200 nm-500 nm的粒度尺寸和很好的单晶结构,其高温超导性具有超导转变温度低、转变温度区间宽、电阻大等性能,此外其还表现出了一定的室温铁磁性,这是由YBCO纳米单晶的小尺寸效应、相滑移机制、高表面离子缺陷浓度、特殊的单晶表面性质等引起的。

关键词： YBa_2Cu_3O_7-x纳米单晶超导性室温铁磁性

钡铪共掺杂钛酸铋钠压电陶瓷制备及铁电性分析

在线全文

学校读者我要写书评

暂无评论

常州大学学报（自然科学版） 2010年第4期22卷 6-10页

作者：韩权威孙玉芳李坤陈王丽华常州大学材料科学与工程学院江苏常州213164 香港理工大学应用物理系及材料研究中心

采用溶胶-凝胶制备工艺制备了(Na0.5Bi0.5)0.935Ba0.065(Ti1-xHfx)O3(x=0.002、0.005、0.01、0.02)无铅压电陶瓷。研究了陶瓷的铁电、压电性能和显微结构。结果表明,随着铪掺杂量的增加,陶瓷晶相转变为4方相,电滞回线发生畸变。对电滞... 详细信息

采用溶胶-凝胶制备工艺制备了(Na0.5Bi0.5)0.935Ba0.065(Ti1-xHfx)O3(x=0.002、0.005、0.01、0.02)无铅压电陶瓷。研究了陶瓷的铁电、压电性能和显微结构。结果表明,随着铪掺杂量的增加,陶瓷晶相转变为4方相,电滞回线发生畸变。对电滞回线的拟合分析表明,有两种铁电畴存在,随温度的升高,电滞回线呈现部分类似于反铁电的特征。该陶瓷体系在x=0.005时,其压电应变常数,径向机电耦合系数,厚度耦合系数,介电常数,介电损耗分别为210pC/N,0.252,0.446,1293,0.055。

关键词：钛酸铋钠无铅压电陶瓷压电性铁电性

在线全文

学校读者我要写书评

暂无评论

基于注意力残差网络的人脸超分辨率重建

计算机工程 2023年第6期49卷 234-241页

作者：王同官赖惠成蔡玉玺高古学汪烈军新疆大学信息科学与工程学院乌鲁木齐830046

为解决通道内部特征信息交互性不足、特征利用和表示不够充分导致的人脸面部细节信息恢复不理想的问题,提出一种基于编码器-解码器的注意力残差网络,并设计基于注意力的残差模块,其主要由基准残差模块、沙漏模块与内部特征拆分注意力模... 详细信息

为解决通道内部特征信息交互性不足、特征利用和表示不够充分导致的人脸面部细节信息恢复不理想的问题,提出一种基于编码器-解码器的注意力残差网络,并设计基于注意力的残差模块,其主要由基准残差模块、沙漏模块与内部特征拆分注意力模块组成,通过内部特征拆分注意力模块加强通道内部之间的交互性,使网络能够提取到更详细的特征信息,恢复出更多人脸面部细节,同时在残差模块中利用一个预激活模块,解决批量归一化层在超分辨率网络中存在的伪影问题。在特征提取单元末端运用多阶特征融合模块充分融合多个阶段的特征,缓解特征在网络传输过程中的丢失现象,提高特征利用率。实验结果表明,该方法可以恢复出更多人脸面部细节,在helen人脸数据集上,重建人脸图像的PSNR值为27.74 dB,相比SISN和DICNet方法,分别提高了1.47 dB、1.12 dB。在CelebA人脸数据集上,重建人脸图像的PSNR值为27.40 dB,相比SISN和DICNet方法,分别提高了1.26 dB、0.39 dB。

关键词：人脸超分辨率注意力机制残差网络特征融合编码器解码器