Electrodeposition and corrosion behavior of Zn-Ni-Mn alloy coatings deposited from alkaline solution

Transactions of Nonferrous Metals Society of China 2020年第2期30卷 548-558页

作者： babak abedini Naghi PARVINI AHMADI Sasan YAZDANI Luca MAGAGNIN Faculty of Materials Engineering Sahand University of TechnologyTabrizIran Dipartimento di Chimica Materiali e Ingegneria Chimica Giulio NattaPolitecnico di MilanoVia Mancinelli 720131MilanoItaly

The potentiostatic electrodeposition of Zn-Ni-Mn was carried out in an alkaline solution with the addition of Mn *** effects of electrolyte Mn2+concentration and deposition potential on the surface morphology,phase structure and corrosion behavior of coatings were *** results of corrosion polarization showed that the presence of higher Mn content in Zn-Ni-Mn coatings could lead to the formation of a good passive layer with a 7-fold increase in Rp of coating and a significant decrease in the corrosion current density compared to those of Zn-Ni *** XRD and the XPS analyses from the surface of Zn-Ni-Mn after corrosion test showed that the passive layer was composed of zinc hydroxide chloride,zinc oxide,zinc hydroxide carbonate,and manganese oxides.

关键词： Zn-Ni-Mn electrodeposition alkaline bath phase structure corrosion resistance chemical composition

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：