Cracking Tendency of Restrained Concrete at Early Ages

在线全文

学校读者我要写书评

暂无评论

Journal of Wuhan University of Technology(Materials Science) 2008年第2期23卷 263-267页

作者： ba hengjing SU Anshuang GAO Xiaojian TAO Qi School of Civil Engineering Harbin Institute of Technology Harbin 150006 China

A modified testing system characterized by full automation, steady operation and high accuracy of strain and stress measurements was developed to determine the cracking tendency of high strength concrete （HSC） in restrained condition at early ages. The shrinkage stress and the tensile creep behavior of HSC at early ages were investigated. The influence of W/C ratio and curing conditions on the early-age shrinkage stress and tensile creep was evaluated. It was found that the lower W/C ratio and drying curing condition resulted in higher shrinkage stress, stress induced tensile creep and greater cracking tendency.

关键词： cracking tendency shrinkage stress tensile creep concrete early ages

Effect of ground granulated blast-furnace slag(GGBFS) and silica fume(SF) on chloride migration through concrete subjected to repeated loading

在线全文

学校读者我要写书评

暂无评论

Science China(Technological Sciences) 2012年第12期55卷 3102-3108页

作者： ZHANG WuMan ba hengjing School of Transportation Science and Engineering Beihang UniversityBeijin g 100191China School of Civil and Engineering Harbin Institute of Technology Harbin 150006China

The effect of ground granulated blast-furnace slag(GGBFS) and silica fume(SF) on the chloride migration through concrete subjected to repeated loading was *** cement was replaced by 20%,30%,40% GGBFS and 5%,10% SF,*** times repeated loadings were applied to specimens,the maximum loadings were 40% and 80% of the axial cylinder compressive strength(f′c),*** migration through concretes was evaluated using the rapid chloride migration test and the chloride concentration in the anode chamber was *** results indicate that the transport number of chloride through concrete containing 20% and 30% GGBFS replacements and 5% and 10% SF replacements is lower than that of the control concrete,but 40% GGBFS replacement increases the transport number of *** loadings at 40% f′cor 80% f′c increase the transport number of chloride for all mixes investigated in this study.5% SF replacement has a very close effect on the chloride permeability of concrete with 20% GGBFS when concrete is subjected to 40% f′cor 80% f′c.

关键词： concrete ground granulated blast-furnace slag (GGBFS) silica fume (SF) chloride migration repeated loading

同方期刊数据库

Hydration of concrete containing calcium-enriched fly ash at subzero temperature

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2007年第S1期26卷 301-305页

作者： ZHAO Yading,ba hengjing,CUI Jinjiang,and HOU Zhiwei School of Materials Science and Engineering,Harbin Institute of Technology,Harbin 150001,China Harbin Inst Technol Sch Mat Sci & Engn Harbin 150001 Peoples R China

The compressive strength,hydration products and microstructure of concrete with calcium-enriched fly ash(CEFA) at different temperature were *** result indicates that the hydration products age of 7 d at-15 ℃ are mainly ettringite and C-S-H,and fly ash particles remain original *** curing was adapted after 7 d curing at-15 ℃.At the age of 35 d,C-S-H was found on the surface of fly ash *** hydration product of CEFA is mainly C-S-H gel,which can densify the microstructure of concrete.

关键词： calcium-enriched fly ash concrete at subzero temperature hydration products

在线全文

学校读者我要写书评

暂无评论

负温防冻剂混凝土的界面显微结构与性能

硅酸盐学报 2007年第8期35卷 1125-1130页

作者：杨英姿巴恒静哈尔滨工业大学材料科学与工程学院哈尔滨150001

研究了不同种类的防冻剂、矿物掺合料对正、负温下水泥净浆、砂浆及混凝土力学性能的影响。通过对比实验表明:水泥净浆、砂浆及混凝土在正、负温条件下抗压强度的变化规律存在显著差异,这取决于其内部显微结构,尤其是界面显微结构的差... 详细信息

研究了不同种类的防冻剂、矿物掺合料对正、负温下水泥净浆、砂浆及混凝土力学性能的影响。通过对比实验表明:水泥净浆、砂浆及混凝土在正、负温条件下抗压强度的变化规律存在显著差异,这取决于其内部显微结构,尤其是界面显微结构的差异。利用显微硬度计、扫描电镜、能谱分析、X射线衍射研究了防冻剂混凝土界面过渡区的范围、元素分布、钙硅比及氢氧化钙的取向度。结果表明:防冻剂能够改善负温下混凝土的界面显微结构,防冻剂和矿物掺合料的复合使用可为负温混凝土提供理想的界面显微结构。

关键词：负温混凝土界面显微结构外加剂

在线全文

学校读者我要写书评

暂无评论

混凝土寿命加速实验方法与预测

硅酸盐学报 2007年第2期35卷 242-246页

作者：巴恒静张武满哈尔滨工业大学土木工程学院哈尔滨150006

基于寿命加速实验的相似理论,采用多通道变电压氯离子渗透实验装置对混凝土进行了加速寿命实验。氯离子的摩尔浓度的负对数(pCl)与其浓度电位呈线性关系。氯离子渗透经过一段非线性阶段后,阳极溶液中氯离子浓度随时间的延长呈线性增加... 详细信息

基于寿命加速实验的相似理论,采用多通道变电压氯离子渗透实验装置对混凝土进行了加速寿命实验。氯离子的摩尔浓度的负对数(pCl)与其浓度电位呈线性关系。氯离子渗透经过一段非线性阶段后,阳极溶液中氯离子浓度随时间的延长呈线性增加。利用寿命加速实验获得的加速曲线,预测氯离子自然渗透达到临界浓度时所需的时间。结果表明:保护层厚度为25mm的混凝土的寿命为25.47～26.38a,该寿命加速实验方法可用于预测混凝土的寿命。

关键词：混凝土寿命加速实验寿命预测多通道变电压氯离子渗透

在线全文

学校读者我要写书评

暂无评论

长期动载下级配碎石的塑性变形与临界应力

同济大学学报（自然科学版） 2010年第9期38卷 1293-1297页

作者：王龙解晓光巴恒静哈尔滨工业大学交通科学与工程学院黑龙江哈尔滨150090 哈尔滨工业大学土木工程学院黑龙江哈尔滨150090

采用中型动三轴仪,在不同围压、不同动应力条件下,研究了级配碎石基层在长期车辆荷载作用下塑性变形的发展规律和分布状态.结果表明,在围压一定时,随着动应力的增加,级配碎石的塑性变形曲线可分为稳定型、衰减型和破坏型,3类塑性变形的... 详细信息

采用中型动三轴仪,在不同围压、不同动应力条件下,研究了级配碎石基层在长期车辆荷载作用下塑性变形的发展规律和分布状态.结果表明,在围压一定时,随着动应力的增加,级配碎石的塑性变形曲线可分为稳定型、衰减型和破坏型,3类塑性变形的分布确定了2个临界状态;临界动应力随围压线性增加,临界动应力比随围压呈对数递减,且两临界应力比在高围压下有趋同态势;级配碎石的塑性变形与动应力水平为指数关系,稳定临界和破坏临界的动应力水平分别为0.79和1.00;典型路面结构应力分析表明,标准荷载下级配碎石过渡层的应力水平为0.72~0.92,小于破坏临界应力水平,级配碎石在长期荷载作用下的塑性变形处于较稳定状态.

关键词：道路工程级配碎石三轴试验塑性变形临界应力

碱矿渣高钙粉煤灰混凝土的优化及长期性能的研究

在线全文

学校读者我要写书评

暂无评论

硅酸盐学报 2000年第Z1期28卷 69-71,75页

作者：唐明巴恒静哈尔滨工业大学哈尔滨150006

碱矿渣混凝土在自然使用环境中的长期稳定性是该材料耐久性研究中的重要课题 .本研究采用碱矿渣激发高钙粉煤灰的活性 ,配制了碱矿渣高钙粉煤灰混凝土 ,重点测试评价了在北方自然环境中存放 8年后的试件力学性能、显微结构及组成 ,综合... 详细信息

碱矿渣混凝土在自然使用环境中的长期稳定性是该材料耐久性研究中的重要课题 .本研究采用碱矿渣激发高钙粉煤灰的活性 ,配制了碱矿渣高钙粉煤灰混凝土 ,重点测试评价了在北方自然环境中存放 8年后的试件力学性能、显微结构及组成 ,综合分析了该材料的长期稳定性 .

关键词：混凝土矿渣粉煤灰长期性能

在线全文

学校读者我要写书评

暂无评论

高性能混凝土早期抗裂试验研究

建筑技术 2008年第1期39卷 59-62页

作者：国爱丽巴恒静哈尔滨工业大学土木工程学院哈尔滨150009

为减少高性能混凝土早期收缩开裂,利用非接触测量技术,通过测量高性能混凝土早期自生及单面干燥条件下的收缩,研究减缩剂、聚丙烯纤维及不同减水剂对高性能混凝土早期自生及干燥收缩的影响。在此基础上,利用板式混凝土早期收缩开裂试验... 详细信息

为减少高性能混凝土早期收缩开裂,利用非接触测量技术,通过测量高性能混凝土早期自生及单面干燥条件下的收缩,研究减缩剂、聚丙烯纤维及不同减水剂对高性能混凝土早期自生及干燥收缩的影响。在此基础上,利用板式混凝土早期收缩开裂试验架,对高性能混凝土进行约束试验,研究减缩剂、减缩剂+聚丙烯纤维等对高性能混凝土早期抗裂的作用。结果表明:减缩剂、聚丙烯纤维、减缩剂+聚丙烯纤维及聚羧酸高效减水剂均有减缩抗裂效果。其作用大小为:减缩剂+聚羧酸高效减水剂>减缩剂+FDN高效减水剂>减缩剂+聚丙烯纤维>聚丙烯纤维。

关键词：高性能混凝土收缩抗裂

在线全文

学校读者我要写书评

暂无评论

二氯甲烷评价混凝土渗透性研究

工业建筑 2005年第6期35卷 66-67,28页

作者：刘志国巴恒静哈尔滨工业大学土木工程学院哈尔滨150006

研究并确立了用二氯甲烷测量混凝土渗透性的参数———浸泡时间t及评价参数ΔG V ,并与ASTMC12 0 7- 97评价混凝土渗透性的方法进行评价参数相关性的比较。结果表明:这两种评价混凝土的渗透性方法的评价参数满足指数函数的形式。

关键词：渗透性混凝土二氯甲烷评价参数浸泡时间甲烷测量指数函数相关性