Evaluation of Impact Strength and Micro-Hardness of Denture Base Acrylic Resin （PMMA） Part Ⅱ

Journal of Chemistry and Chemical Engineering 2010年第12期4卷 52-56页

作者： Saied Hamad Mohamed Tawfik Ajaal albasheir musbah al-jadi Faculty of Dentistry Prosthodontic Department AI-Arab Medial Benghazi Libya Academic of Postgraduate Studies-Biomedical Engineering Department Tripoli Libya

Poly （methyl methacrylate） is widely used as denture base material. During fabrication of a denture, the physical and mechanical properties are influenced by cure condition. Each cure cycle or fabrication technique is attempts to optimize the properties for a given application. The aim of this study was to compare two types of commercially available denture base materials （heat-cure and self-cure） in their mechanical properties. The samples were prepared according to the daily routine work for sample preparation in dental laboratories. After reaching dough stage the mix packed into dumbbell shaped of stainless steel mould and pressed in a hydraulic bench press for 25 mins at room temperature. For heat cure the polymerization cycle was carried out using water bath, while self cure was done at room temperature. The impact strength was evaluated using Charpy impact test. The hardness test was conducted using a calibrated Vickers hardness tester machine. The lowest impact strength was observed in self-cure denture base material （self cure material 6.2 kJ/m^2 while heat cure 12.69 kJ/m^2. It appears that the tendency of heat cure to fracture was lower than self-cure denture base materials. Heat cure denture base material has significantly higher hardness test values than self-cure denture base material. The observed VHN value of the heat-cure was 20.09 g/mm^2 while the self-cure value was 12.7 g/mm^2. This is may be due to the plasticizer effect of residual monomer which was higher in self curing material as reported in previous work. Generally, the heat cure material showed better properties compared to self cure material.

关键词： Impact strength micro-hardness denture base materials.

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：