Transactions of Nonferrous Metals Society of China 2022年第2期32卷 540-558页

作者： J.CHÁVEZ O.JIMÉNEZ D.BRAVO-BARCENAS L.OLMOS F.ALVARADO-HERNÁNDEZ M.A.GONZÁLEZ a.bedolla-jacuinde M.FLORES Departamento de Ingeniería Mecánica Eléctrica CUCEIUniversidad de GuadalajaraBlvd.Marcelino García Barragán#1421GuadalajaraC.P.44430México Departamento de Ingeniería de Proyectos CUCEIUniversidad de GuadalajaraJoséGuadalupe Zuno#48Los BelenesZapopanC.P.45150México Departamento de Ingeniería de Proyectos CUCEIUniversidad de Guadalajara-CONACyTBlvd.Marcelino García Barragán#1421GuadalajaraC.P.44430México Instituto de Investigaciones en Ciencias de la Tierra INICITUniversidad Michoacana de San Nicolás de HidalgoAv.Francisco J.Mujica S/NCiudad UniversitariaMoreliaMichoacánC.P.58030México Unidad Académica de Ingeniería I Universidad Autónoma de ZacatecasAv.López Valverde 801ZacatecasZacatecasC.P.98060México Instituto de Investigaciones Metalúrgicas IIMMUniversidad Michoacana de San Nicolás de HidalgoEdificio‘‘U-5’’Ciudad UniversitariaMoreliaMichoacánC.P.58030México

用固相烧结法制备Ti6Al4V/xTiN(x=0,5,10,15,体积分数,%)复合材料,研究材料的腐蚀与腐蚀磨损行为及其与显微组织和显微硬度的关系。采用37℃和模拟体液模拟人体环境。结果表明,当TiN含量为15%时,氮(N)固溶到钛(Ti)晶格中使α-Ti稳定化,... 详细信息

用固相烧结法制备Ti6Al4V/xTiN(x=0,5,10,15,体积分数,%)复合材料,研究材料的腐蚀与腐蚀磨损行为及其与显微组织和显微硬度的关系。采用37℃和模拟体液模拟人体环境。结果表明,当TiN含量为15%时,氮(N)固溶到钛(Ti)晶格中使α-Ti稳定化,该显微组织的改变使Ti64基体的硬化效应达到58%。随着TiN颗粒的加入,复合材料的腐蚀电位变得更高,而腐蚀电流密度受残余孔隙率的影响而增大,使材料的耐腐蚀性降低。然而,含15%TiN样品的钝化行为减弱。复合材料的非钝化行为导致其在腐蚀磨损测试过程中电位降低。此外,固溶强化使复合材料的磨损率降低88%。研究结果有利于理解材料的成分和烧结参数与提高腐蚀磨损性能之间的关系。

关键词： Ti64合金复合材料粉末冶金显微组织腐蚀腐蚀磨损

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Effect of V-Ti on the Microstructure and Abrasive Wear Behavior of 6CrC Cast Steel Mill Balls

引用

Journal of Minerals and Materials Characterization and Engineering 2014年第5期2卷 383-391页

作者： S. I. Maldonado-Ruiz P. Orozco-González V. H. Baltazar-Hernández A. bedolla-jacuinde M. A. L. Hernández-Rodríguez Instituto de Investigaciones Metalúrgicas Universidad Michoacana Morelia México Unidad Académica de Ingeniería Universidad Autónoma de Zacatecas Zacatecas México Universidad Autónoma de Nuevo León Monterrey México

Iron-chromium cast alloys are basically abrasive wear resistant materials particularly employed in mining industry;these alloys are often utilized in the manufacture of milling balls. In particular, high Cr and high C cast alloys have been subjected of significant research;for instance, most reports have been addressed on analyzing the relation between microstructure and the abrasive wear behavior;however, there exist a reduced number of reports on relatively low Cr and low C cast alloys. In this research, five low Cr cast steels containing additions of V and Ti were melted in an open atmosphere induction furnace. Comparisons on the morphology, size, type and distribution of carbides were carried through optical microscopy, SEM and XRD. Hardness testing was employed at room temperature with the purpose of correlate to wear behavior. A laboratory pilotplant ball-mill set with a batch of ore was utilized in order to evaluate the abrasive wear resistance. According to microstructure observations, a martensitic primary matrix was revealed in all specimens. The fraction of M7C3 and M3C interdendritic eutectic carbides varied according to alloying level. Further results indicated that variations in the shape and size of M7C3 and M3C along with the presence of V and Ti carbides influenced on the abrasive wear behavior of low Cr cast steel mill balls.

关键词： Wear-Resistance Grinding-Media Cr-C Cast-Steel

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：