锂离子二次电池正极材料LiVPO_4F的制备及其电化学性能的研究

在线全文

学校读者我要写书评

暂无评论

无机化学学报 2005年第10期21卷 1597-1600页

作者：李宇展任俊霞周震高学平阎杰南开大学新能源材料化学研究所天津300071

A new cathode material, LiVPO4F, has been synthesized through two steps of solid-state reactions. In the first step, vanadium pentoxide, ammonium dihydrogen phosphate, and a high surface area carbon were pre-heated at 300 ℃ and reacted at 750 ℃ under an inert atmosphere to yield the trivalent vanadium phosphate VPO4. In the second step, the product LiVPO4F was synthesized by the reaction with VPO4 and LiF. The LiVPO4F was characterized by X-ray diffraction, scanning electron microscopy, cyclic voltammetry and charge/discharge testing measurements. The LiVPO4F is triclinic crystalline system. At 0.1 C rate, the first charge/discharge capacities were 150.1 mAh·g-1 and 132.6 mAh·g-1; At 0.2 C rate, the first charge/discharge capacities were 142.9 mAh·g-1 and 125.2 mAh·g-1. The LiVPO4F from this work has higher charge/discharge voltage 4.3 V and 4.1 V, respectively.

关键词：锂离子二次电池正极材料氟磷酸钒锂电化学性能

在线全文

学校读者我要写书评

暂无评论

草酸电还原反应机理的研究

电化学 2004年第1期10卷 41-45页

作者：刘欣李宇展胡瑞省顾登平河北师范大学化学学院河北石家庄050016

　以硫酸钠溶液作底液,用快速循环伏安和电势阶跃法研究了草酸在铅电极上的电还原机理,测定了草酸电还原第一步反应的动力学参数,并根据循环伏安图比较相同条件下草酸,乙醛酸和乙醇酸的还原峰峰电势,推断出草酸还原的中间产物.研究结果... 详细信息

　以硫酸钠溶液作底液,用快速循环伏安和电势阶跃法研究了草酸在铅电极上的电还原机理,测定了草酸电还原第一步反应的动力学参数,并根据循环伏安图比较相同条件下草酸,乙醛酸和乙醇酸的还原峰峰电势,推断出草酸还原的中间产物.研究结果表明,草酸电还原遵从不可逆2电子EE反应机理.

关键词：草酸电还原反应反应机理快速循环伏安法电势阶跃法不可逆2电子EE反应动力学参数乙醛酸乙醇酸中间产物

在线全文

学校读者我要写书评

暂无评论

草酸电还原研制乙醇酸

河北师范大学学报（自然科学版） 2003年第4期27卷 385-387页

作者：李宇展刘伟顾登平河北师范大学化学学院河北石家庄050016 沧州师范专科学校化学系河北沧州061001

采用循环伏安 (CV)法确定了草酸可以还原为乙醇酸 ,以铅作阴极材料的阳离子交换膜电解槽 ,电解草酸研制乙醇酸 ,并且以电流密度、电量、温度和电解液的流速做了 4因素 4水平的正交实验 ,得出了最佳工艺条件 ,产率达

关键词：乙醇酸电化学还原草酸循环伏安法阳离子交换膜电解槽电流密度电量电解温度

Effect of Lu_2O_3 on Charge/discharge Performances of Spherical Nickel Hydroxide at High Temperature

在线全文

学校读者我要写书评

暂无评论

Journal of Rare Earths 2005年第6期23卷 732-736页

作者：任俊霞王小建李宇展高学平阎杰 Institute of New Energy Material Chemistry Nankai University Tianjin 300071 China Institute

Nickel-metal hydride （Ni/MH） batteries are one of promising batteries for electric vehicle applications, but at high temperature the charge efficiency of nickel electrode is very low. In order to improve the high-temperature-efficiency of nickel electrode, spherical nickel hydroxide mixed with various ratios of Lu2O3 was used as active material of pasted nickel electrodes. The results of charge/discharge experiments, cyclic voltammetric measurements and XRD characterizations have shown that after addition of Lu2O3, the oxygen evolution overpotcntial is elevated much, the charge efficiency of nickel electrode at high temperature is greatly improved and the content of β-NiOOH phase increases in charged electrodes. In addition, the mixed ratio of Lu2O3 has different effects on high temperature performances of nickel electrode at different charge/discharge currents, 3.5 % is the optimum mixed ratio, and the action of Lu2O3 on high temperature electrochemical behaviors is more apparent when nickel electrodes are charged at small current than large current.

关键词： spherical nickel hydroxide high temperature performances Lu2O3 oxygen evolution overpotential rare earths

Lu_2O_3对球形Ni(OH)_2高温充放电性能的影响

在线全文

学校读者我要写书评

暂无评论

中国稀土学报 2005年第2期23卷 195-199页

作者：任俊霞王小建李宇展高学平阎杰南开大学新能源材料化学研究所天津300071

为了改善镍电极的高温充电效率,采用机械混合的方式将球形Ni(OH)2与不同比例的Lu2O3混合后制成粘结式镍正极。充放电测试、循环伏安和XRD等实验结果表明,掺杂Lu2O3后镍电极的析氧过电位明显提高,高温充电效率得到了很大改善,在充电后的... 详细信息

为了改善镍电极的高温充电效率,采用机械混合的方式将球形Ni(OH)2与不同比例的Lu2O3混合后制成粘结式镍正极。充放电测试、循环伏安和XRD等实验结果表明,掺杂Lu2O3后镍电极的析氧过电位明显提高,高温充电效率得到了很大改善,在充电后的电极中βNiOOH生成;而且Lu2O3的掺杂比例对镍电极的高温性能在不同的充放电倍率下有不同程度的影响,3.5%是最好的掺杂比例,掺杂对高温小电流充电效率的改善作用要大于高温大电流充电。

关键词：球形Ni(OH)2 高温性能 Lu2O3 析氧过电位稀土

在线全文

学校读者我要写书评

暂无评论

锂离子蓄电池钒系正极材料的研究进展

电源技术 2005年第2期29卷 124-127页

作者：李宇展任慢慢吴青端魏进平阎杰南开大学新能源材料化学研究所天津300071

锂离子蓄电池具有很多的优良特性,发展很快并得到了广泛地应用。其中锂离子蓄电池正极材料的研究主要集中在第四周期过渡金属的嵌锂氧化物LiCoO2、LiNiO2、LiCoxNi1-xO2、LiCo1/3Ni1/3Mn1/3O2、LiMnO2、LiMn2O4、LiFePO4上。近年来,钒... 详细信息

锂离子蓄电池具有很多的优良特性,发展很快并得到了广泛地应用。其中锂离子蓄电池正极材料的研究主要集中在第四周期过渡金属的嵌锂氧化物LiCoO2、LiNiO2、LiCoxNi1-xO2、LiCo1/3Ni1/3Mn1/3O2、LiMnO2、LiMn2O4、LiFePO4上。近年来,钒系正极材料的研究引起了人们的广泛关注。文章对嵌锂钒系化合物LiV3O8,LiNiVO4,Li3V2(PO4)3和LiVPO4F等正极材料的制备方法、结构及电化学性能的研究现状进行了综述。

关键词：锂离子蓄电池正极材料锂钒化合物

在线全文

学校读者我要写书评

暂无评论

草酸电还原制乙醇酸化学分析方法的研究

河北师范大学学报（自然科学版） 2003年第6期27卷 599-601页

作者：李宇展刘艳春顾登平河北师范大学化学学院河北石家庄050016

草酸阴极还原制乙醇酸的电解液可用简便的化学分析方法测定,其中草酸的定量可以钙盐沉淀后用高锰酸钾法测定;乙醛酸的定量用国家标准附以酸度计控制终点来测定;乙醇酸的定量用邻苯二甲酸酐来测定.本化学分析方法具有快速、简单、可靠的... 详细信息

草酸阴极还原制乙醇酸的电解液可用简便的化学分析方法测定,其中草酸的定量可以钙盐沉淀后用高锰酸钾法测定;乙醛酸的定量用国家标准附以酸度计控制终点来测定;乙醇酸的定量用邻苯二甲酸酐来测定.本化学分析方法具有快速、简单、可靠的特点,具有重要的工业价值.

关键词：乙醇酸化学分析方法草酸阴极电化学还原反应有机电合成

微波法合成正极材料Li_3V_2(PO_4)_3

在线全文

学校读者我要写书评

暂无评论

电池 2006年第1期36卷 13-14页

作者：任慢慢李宇展周震高学平阎杰南开大学新能源材料化学研究所天津300071

用微波法合成了锂离子电池正极材料Li3V2(PO4)3。XRD、充放电和循环伏安测试表明:在900℃下恒温11 min,合成的样品结晶度好、无杂相,0.2C时,使用该材料的电池首次循环的充、放电容量分别为177.1 mAh/g和145.7 mAh/g,循环50次后,放电容量... 详细信息

用微波法合成了锂离子电池正极材料Li3V2(PO4)3。XRD、充放电和循环伏安测试表明:在900℃下恒温11 min,合成的样品结晶度好、无杂相,0.2C时,使用该材料的电池首次循环的充、放电容量分别为177.1 mAh/g和145.7 mAh/g,循环50次后,放电容量为98 mAh/g。当充电到4.9 V时,Li3V2(PO4)3存在4个充电平台,且有较高的放电平台。

关键词：微波加热 Li3V2(PO4)3正极材料充放电容量锂离子电池

在线全文

学校读者我要写书评

暂无评论

分光光度法测定水杨酸的含量

河北师范大学学报（自然科学版） 2002年第6期26卷 606-608页

作者：焦丽芳李宇展顾登平张宏坤河北师范大学化学学院河北石家庄050016

水杨酸与醋酸铜在 p H为 5 .8～ 6.0时 ,能迅速形成 1种稳定的黄绿色络合物 ,此络合物在波长40 0 nm处有最大吸收 ,ε为 2 0 1 L/(cm· mol) ,在 0 .2～ 4.0 mg/m L范围内遵守比耳定律 ,并能稳定 3 0 h.在以水杨酸为原料电化学还原制备... 详细信息

水杨酸与醋酸铜在 p H为 5 .8～ 6.0时 ,能迅速形成 1种稳定的黄绿色络合物 ,此络合物在波长40 0 nm处有最大吸收 ,ε为 2 0 1 L/(cm· mol) ,在 0 .2～ 4.0 mg/m L范围内遵守比耳定律 ,并能稳定 3 0 h.在以水杨酸为原料电化学还原制备水杨醛的电解液中 ,水杨醛和硼酸影响此络合物的吸光度。

关键词：分光光度法水杨酸醋酸铜水杨醛含量测定电解液香料生产