非负载和氧化铝负载的纳米CeO_2-ZrO_2和CeO_2-Te_2O_3固溶体催化CO氧化(英文)

作     者：M.Reddy BENJARAM Thrimurthulu GODE Lakshmi KATTA 

作者机构：Inorganic and Physical Chemistry DivisionIndian Institute of Chemical Technology 

出 版 物：《催化学报》 (CHINESE JOURNAL OF CATALYSIS)

年 卷 期：2011年第32卷第5期

页      面：800-806页

核心收录：

学科分类：081705[工学-工业催化] 08[工学] 0817[工学-化学工程与技术] 0703[理学-化学] 

基　　金：supported by Council of Scientific and Industrial Research(CSIR) New Delhi India 

主　　题：ceria zirconia terbia alumina-support deposition coprecipitation CO oxidation 

摘      要：Ceria-zirconia(CZ)and ceria-terbia(CT)and alumina-supported ceria-zirconia(CZA)and ceria-terbia(CTA)solid solutions were synthesized by coprecipitation and deposition precipitation methods,respectively.Structural characteristics and catalytic activity of the synthesized samples have been investigated using X-ray diffraction(XRD),high resolution transmission electron microscopy(HRTEM),X-ray photoelectron spectroscopy(XPS),Raman spectroscopy(RS),and Brunauer-Emmett-Teller(BET)surface area measurements.To evaluate the catalytic properties,total oxygen storage capacity and CO oxidation activity measurements were carried out.The XRD analyses revealed the formation of Ce0.75Zr0.25O2 phase for CZ and Ce0.5Zr0.5O2 and Ce0.6Zr0.4O2 phases for CZA samples,respectively.While the formation of only Ce0.8Tb0.2O2-δphase was noted for both CT and CTA samples.All the supported and unsupported samples adopted a fluorite-type structure and exhibited cell parameters with respect to Vegard s rule.The HRTEM results indicated well-dispersed particles of the size around 5 nm.The RS measurements suggested the presence of oxygen vacancies due to defective structure formation.The XPS studies revealed the presence of cerium in both Ce 4+ and Ce 3+ oxidation states in different proportions.It was found that CO oxidation for CTA occurs at very much lower temperature than CT,CZ,and CZA samples.Details of these findings by correlating with the structural characterization studies are consolidated.