Effect of sintering temperature on the dielectric,ferroelectric and energy storage properties of SnO_(2)-doped Bi_(0.5)(Na_(0.8)K_(0.2))_(0.5)TiO_(3)lead-free ceramics

作     者：Nguyen Truong-Tho Le Dai Vuong 

作者机构：Department of PhysicsCollege of Sciences Hue UniversityHue CityVietnam Faculty of Natural Sciences Thu Dau Mot University Binh Duong ProvinceVietnam 

出 版 物：《Journal of Advanced Dielectrics》 (先进电介质学报（英文）)

年 卷 期：2020年第10卷第4期

页      面：13-21页

学科分类：081702[工学-化学工艺] 0808[工学-电气工程] 0809[工学-电子科学与技术（可授工学、理学学位）] 0817[工学-化学工程与技术] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0702[理学-物理学] 

基　　金：This research was funded by Ministry of Education and Training under Grant No.B2019-DHH-13 

主　　题：Lead-free ceramics BNKT sintering temperature dielectric constant 

摘      要：Sintered lead-free Bi_(0.5)(Na_(0.8)K_(0.2)T_(0.5)(Ti0:96Sn0:04TO_(3)ceramics(BNKTS)have been fabricated via a solid-state *** effect of sintering temperature on the structural,morphological,dielectric,ferroelectric and energy storage properties of BNKTS ceramics was investigated,and it was found that the electrical properties of the synthesized ceramics increased with the increase in the sintering temperature,and the highest values were achieved at 1100℃.The ceramics sintered at the optimized temperature of 1100℃exhibited the best physical,dielectric,ferroelectric and energy storage properties,namely,high density(the relative density,ρ=5:88 ***^(-3),approximate to 96.7%of the theoretical value),high densification factor(DF=0:93),high dielectric constant(ε_(r)=1215),low dielectric loss(tanδ=0:051),highest dielectric constant(ε_(max)=4335),high remanent polarization(Pr=9:5μ***^(-2),high coercive field(E_(c)=14:3 kV/cm),high energy storage density(0.12 J/cm^(3),and high energy storage efficiency(41.7%at 46.3 kV/cm).