High-Frequency Induction Heating of Needle-Shaped Mg-Ferrite for Ablation Therapy of Human Cancer
High-Frequency Induction Heating of Needle-Shaped Mg-Ferrite for Ablation Therapy of Human Cancer作者机构:Graduate School of Science and EngineeringEhime University Department of Environmental Materials EngineeringNiihama National College of Technology Department of Electronic Control EngineeringNiihama National College of Technology Department of SurgeryGraduate School of MedicineEhime University
出 版 物:《Journal of Iron and Steel Research(International)》 (钢铁研究学报(英文版))
年 卷 期:2012年第19卷第S2期
页 面:735-738页
核心收录:
学科分类:0831[工学-生物医学工程(可授工学、理学、医学学位)] 08[工学] 0836[工学-生物工程]
基 金:Item Sponsored by a Grant-in-Aid from Ministry of Education Science Sports and Culture of Japan[No.23500559:Naohara T]
主 题:high-frequency induction heating cancer therapy ablation treatment eddy current loss residual loss
摘 要:For application as a novel ablation therapy of human cancer,the heating property of a needle-shaped Mg-ferrite prepared by a sintering technique was studied in a high-frequency induction field at 370 *** inserted into cylindrical clay,the increase in temperature(Δ7)was 31.2℃ for the specimen with a 1.5 mm diameter,while the 1.0mm diameter specimen exhibited a ΔT value of 15.7℃ after the induction time of *** ΔT exhibited a high value of 57.9℃ during the simultaneous insertion of 3 1.5mm diameter *** the computer simulation images, the relatively lower magnetic flux density and concurrent neghgibly low current density were observed from the surface to the internal regions,being different from the behavior of a ferromagnetic Ni-rod with the same size.