Preparation and Characterization of Poly(vinyl alcohol)/ZIF-8 Porous Composites by Ice-templating Method with High ZIF-8 Loading Amount
Preparation and Characterization of Poly(vinyl alcohol)/ZIF-8 Porous Composites by Ice-templating Method with High ZIF-8 Loading Amount作者机构:School of Materials Science and EngineeringBeijing Institute of TechnologyBeijing 100081China
出 版 物:《Chinese Journal of Polymer Science》 (高分子科学(英文版))
年 卷 期:2020年第38卷第6期
页 面:638-643页
核心收录:
学科分类:07[理学] 08[工学] 070304[理学-物理化学(含∶化学物理)] 0817[工学-化学工程与技术] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学]
主 题:Poly(vinyl alcohol) ZIF-8 Ice-templating Porous composite C02 adsorption
摘 要:A bulk Poly(vinyl alcohol)/ZIF-8(PVA/ZIF-8)porous composite with aligned porous structure was prepared by ice-templating method.The microstructure of PVA/ZIF-8 porous composites was characterized by scanning electron microscopy(SEM).The results showed that the composites had regular pore structure and ZIF-8 nanoparticles were evenly distributed on the skeleton of PVA.X-ray diffraction(XRD)test results showed that the crystalline structure of ZIF-8 was well preserved in the composites.The specific surface area of the composite was characterized by nitrogen adsorption/desorption test.The specific surface area of the composite was up to 1160 m^2 g^1.PVA/ZIF-8 porous composites could also support a certain weight with almost no volume shrinkage.The carbon dioxide adsorption quantity of the composite was up to 11.3 cm^3 g^1,proving that PVA/ZIF-8 porous composite has a good application prospect in the field of carbon dioxide adsorption.