Effects of plating factors on morphology and appearance of electrogalvanized steel sheets

作     者：Hiroaki N AKANO 

作者机构：Department of Materials Science and EngineeringFaculty of EngineeringKyushu University 

出 版 物：《中国有色金属学会会刊：英文版》 (Transactions of Nonferrous Metals Society of China)

年 卷 期：2009年第19卷第4期

页      面：835-841页

核心收录：

学科分类：080503[工学-材料加工工程] 0806[工学-冶金工程] 08[工学] 0818[工学-地质资源与地质工程] 0815[工学-水利工程] 0805[工学-材料科学与工程（可授工学、理学学位）] 0813[工学-建筑学] 0703[理学-化学] 0814[工学-土木工程] 0702[理学-物理学] 

主　　题：电镀锌钢板 外观 形态 

摘      要：Because the lightness,the gloss and the press-formability of electrogalvanized steel sheets change depending on the morphology of deposited Zn,control of this factor is essential to improving these *** effects of plating factors on the morphology of deposited Zn were systematically discussed both from the crystallographic viewpoint of epitaxy between Zn and steel and from the electrochemical viewpoint of the overpotential for Zn *** factors include crystal orientation of steel substrate,current density,flow rate,temperature,addition of inorganic compounds to the solution and pre-adsorption of organic *** plating factors affect the overpotential for Zn deposition and epitaxy between Zn and *** crystal orientation index of the Zn basal plane and the platelet crystal size of Zn are decreased with increasing the overpotential for Zn *** are also decreased with decreasing the epitaxy between Zn and steel,even when the overpotential is kept *** the overpotential for Zn deposition is increased,the surface roughness of deposited Zn increases because of an increase in the inclination of the Zn basal plane to the steel *** the epitaxy between Zn and steel is decreased without changing the overpotential,the surface roughness is reduced due to the decrease in platelet crystal size of Zn,although the inclination of the Zn basal plane is somewhat *** lightness of deposited Zn is enhanced with decreasing the surface roughness of Zn.