Interlaminar Fracture Toughness of Epoxy Glass Fiber Fly Ash Laminate Composite

作     者：Ajit Bhandakkar Niraj Kumar R. C. Prasad Shankar M. L. Sastry 

作者机构：Department of Metallurgical Engineering and Materials Science Indian Institute of Technology Bombay Mumbai India Mechanical Aerospace and Structural Engineering Washington University in St. Louis Saint Louis USA 

出 版 物：《Materials Sciences and Applications》 (材料科学与应用期刊（英文）)

年 卷 期：2014年第5卷第4期

页      面：231-244页

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：Interlaminar Fracture Toughness Epoxy Glass Fiber Laminate Composite Fly Ash 

摘      要：Epoxy glass fiber laminate composite (PMCs) are finding ever increasing applications in aerospace and automobile industries due to its high strength to weight ratio and resistance to aqueous environment. Additions of particulate reinforcements in the polymer matrix are reported to improve the Interlaminar Shear Strength and Interlaminar Fracture Toughness of the composites. In the present investigation, epoxy glass fiber laminate composites were processed using hand layup and vacuum bagging technique. The particulate reinforcement precipitator fly ash (25 - 45 μm) was added in the epoxy matrix by mechanical mixing up to 10 wt%. The effects of fly ash reinforcement on the mechanical properties and Interlaminar Fracture Toughness were studied before and after exposure to aqueous fog in a salt fog chamber at 45°C. In unexposed condition Mode I interlaminar fracture toughness of epoxy glass fiber laminate composite improved by the addition of fly ash reinforcement 10% (By weight) by 49.43% and when it was subjected to aqueous fog for 10 days the interlaminar fracture toughness improved 58.42%. Exposure to aqueous fog for 10 days causes plasticization of resin matrix and weakening of fiber/matrix interface results in improvement in interlaminar fracture toughness. The fracture surfaces were analyzed using scanning electron microscopy.