Effect of slag composition on the cleanliness of 28MnCr5 gear steel in the refining processes

作     者：Wen-liang Dong Hong-wei Ni Hua Zhang Ze-an Lü 

作者机构：The State Key Laboratory of Refractories and MetallurgyWuhan University of Science and TechnologyWuhan 430081China Shougang Research Institute of TechnologyBeijing 100043China 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2016年第23卷第3期

页      面：269-275页

核心收录：

学科分类：080602[工学-钢铁冶金] 08[工学] 0806[工学-冶金工程] 

基　　金：financially supported by the Program for New Century Excellent Talents in Universities of China(No.NCET-07-0650) 

主　　题：gear steel refining cleanliness slag composition electromotive force 

摘      要：The equilibrium reaction between CaO-Al2O3-SiO2-MgO slag and 28MnCr5 molten steel was calculated to obtain the suitable slag composition which is effective for decreasing the oxygen content in molten steel. The dissolved oxygen content [O] in molten steel un- der different top slag conditions was calculated using a thermodynamic model and was measured using an electromotive force method in slag-steel equilibrium experiments at 1873 K. The relations among [O], the total oxygen content （T.O）, and the composition of the slag were investigated. The experimental results show that both [O] and T.O decrease with decreasing SiO2 content of the slag and exhibit different trends with the changes in the CaO/Al2O3 mass ratio of the slag. Increasing the CaO/Al2O3 mass ratio results in a decrease in [O] and an in- crease in T.O. To ensure that T.O ≤ 20 ppm and [O] ≤ 10 ppm, the SiO2 content should be controlled to 〈5wt%, and the CaO/AI203 mass ratio should be in the range from 1.2 to 1.6.