Large-area growth of ultra-high-density single-walled carbon nanotube arrays on sapphire surface

作     者：Lixing Kang Yue Hu Hua Zhong Jia Si Shuchen Zhang Qiuchen Zhao Jingjing Lin Qingwen Li Zhiyong Zhang Lianmao Peng Jin Zhang 

作者机构：Division ofAdvanced Nanomaterials Suzhou Institute of Nanotech and Nanobionics Chinese Academy of Sciences Suzhou 215123 China Center for Nanochemistry Beijing Science and Engineering Technology Research Center for Low Dimensional Carbon Materials College of Chemistry and Molecular Engineering Peking University Beijing 100871 China University of ChineseAcademy of Sciences Beijing 100049 China 4 Key Laboratory for the Physics and Chemistry of Nanodevices Department of Electronics Peking University Beijing 100871 China Key Laboratory for the Physics and Chemistry of Nanodevices Department of Electronics Peking University Beijing 100871 China 

出 版 物：《Nano Research》 (纳米研究（英文版）)

年 卷 期：2015年第8卷第11期

页      面：3694-3703页

核心收录：

学科分类：0808[工学-电气工程] 0809[工学-电子科学与技术（可授工学、理学学位）] 07[理学] 070205[理学-凝聚态物理] 08[工学] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程（可授工学、理学学位）] 081201[工学-计算机系统结构] 0702[理学-物理学] 0812[工学-计算机科学与技术（可授工学、理学学位）] 

基　　金：Acknowledgements This work was supported by the National Natural Science Foundation of China (Nos. 21233001  21129001  51272006  51432002  and 51121091)  the National Basic Research Program of China (No. 2011CB932601) and Beijing Municipal Science and Technology Commission (No. D141100000614001) 

主　　题：单壁碳纳米管 碳纳米管阵列 超高密度 可控生长 蓝宝石 表面 面积 催化剂结构 

摘      要：获得高密度的、大区域的围单人赛的碳 nanotube (SWNT ) 的可伸缩的途径穿的 A 为在实际电子设备认识到 SWNT 的完整的潜力是必要的；这仍然是大挑战。这里，我们由联合特洛伊催化剂在蓝宝石表面上为 ultra-high-density SWNT 数组的大区域的生长报导一个改进合成方法(免除了底层，保证超离频密度) 与瞬间 nanoparticles (在表面上装载了，稳定释放特洛伊催化剂) 作为合作催化剂。稠密、非常排列的 SWNT 盖住全部底层，本地密度象 160 tubes/m 一样高。在如此的数组上造的地效果晶体管(联邦货物税) 在排水管来源电压给了 488 A/m 的产量电流密度(V ds )= 门来源电压(V gs )=2 V，相应于在传导力上每 244 S/m 的宽度。这些结果在 SWNT 的控制结构的生长证实特洛伊瞬间催化剂的潜在的应用的宽范围。