Texture of Cold Rolled Strip of Fe-3Si Steel Produced by Thin Slab Casting and Rolling

作     者：LI Chang-sheng YANG Hua WANG Yan-fang YU Yong-mei 

作者机构：State Key Laboratory of Rolling and AutomationNortheastern UniversityShenyang 110004LiaoningChina Shougang Qian'an Iron and Steel CorporationQian'an 064404HebeiChina 

出 版 物：《Journal of Iron and Steel Research International》 (国际钢铁研究杂志)

年 卷 期：2011年第18卷第3期

页      面：40-46页

核心收录：

学科分类：080503[工学-材料加工工程] 080602[工学-钢铁冶金] 08[工学] 0806[工学-冶金工程] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

基　　金：Item Sponsored by National Natural Science Foundation of China(50534020) 

主　　题：silicon steel texture hot rolling cold rolling thin slab continuous casting direct rolling 

摘      要：The hot rolled strip of Fe-3Si steel was experimentally produced by thin slab casting and rolling（TSCR） process in the *** texture evolution rule was investigated during hot rolling and cold *** texture distribution of cold rolled strips with four kinds of cold rolling reduction schedules was observed through X-ray diffraction method,and the orientation density variation of 1/16 layer,1/8 layer,1/4 layer,and 1/2 layer in thickness was *** cold rolled texture of steel A with four kinds of cold rolling reduction schedules was mainly composed of α and γ *** rolling reduction ratio of 70% was more beneficial for obtaining more γ *** γ fiber texture orientation density of {111}01-1 and {111}1-1-2 was the largest on the 1/8 layer and 1/4 layer and the least on the 1/16 layer and 1/2 layer for steel *** texture orientation density of {001}-{223}11-0 in the α fibers for steel C was increased,but the texture orientation density of {332}-{110}11-0 was low.