Asymmetric cast-rolling of 1050 aluminum alloy strip under multi-energy field

作     者：石琛 毛大恒 扶宗礼 Chen SHI;Da-heng MAO;Zong-li FU

作者机构：中南大学材料科学与工程学院长沙410083 中南大学高性能复杂制造国家重点实验室长沙410083 

出 版 物：《Transactions of Nonferrous Metals Society of China》 (中国有色金属学报（英文版）)

年 卷 期：2014年第24卷第9期

页      面：2815-2823页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

基　　金：Project(2014CB046702)supported by National Basic Research Program of China 

主　　题：aluminum alloy 1050 asymmetric cast-rolling multi-energy field microstructure mechanical properties 

摘      要：Technological parameters of asymmetric cast-rolling under multi-energy field were investigated on horizontal twin roll caster（d400 mm×500 mm）, and their effects on structures and properties of 1050 strips were analyzed by comparing with traditional cast-rolling. Results show that when length of cast-rolling area is 70 mm, melt temperature of head box is 670 °C, cast rolling speed is 1.3 m/min, exciting current is 10 A, center frequency is（13±1） Hz, ultrasonic power is 200 W and ultrasonic frequency is（20±0.2） kHz, the 1050 strip with the best microstructure can be prepared successfully; its center segregated layer disappears; the average grain size is reduced by about 40%; the crystal grains are distributed evenly; micro segregation decreases obviously; the precipitated phases are distributed along the grain boundaries evenly; and the tensile strength, yield strength, elongation and micro-hardness of cast-rolled strip are improved by 22.6%, 23.66%, 38.75% and 9.90%, respectively.