Improvement of Wear Resistance of Magnesium Alloy AZ91HP by High Current Pulsed Electron Beam Treatment
Improvement of Wear Resistance of Magnesium Alloy AZ91HP by High Current Pulsed Electron Beam Treatment作者机构:StateKeyLab.ofMaterialssurfaceModificationbyLaserIonandElectronBeamsDatianChina StateKeyLab.ofMaterialssurfaceModificationbyLaserIonandElectronBeamsDatianChina//DepartmentofMaterialsEngineeringDalianUniversityofTechnologyDalianChina
出 版 物:《材料热处理学报》 (Transactions of Materials and Heat Treatment)
年 卷 期:2004年第25卷第5B期
页 面:1029-1031页
核心收录:
学科分类:08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0802[工学-机械工程] 0704[理学-天文学] 080201[工学-机械制造及其自动化] 0702[理学-物理学]
主 题:镁合金 HCPEB 磨损性能 AZ91HP 表面改性 高电流脉冲电子束
摘 要:Surface modification of magnesium alloy AZ91HP (9wt%Al, 0.5wt%Zn, 0.5wt%Mn, Mg remaining percentage) by high current pulsed electron beam (HCPEB) treatment was studied in this paper. The secondary phase MgnAln is nearly completely dissolved and as a result, a super-saturated solid solution forms on the re-melted surface. The microhardness is increased both in and far beyond the heat-affected zone (HAZ), reaching about 250um. Measurements on sliding wear have shown that the wear resistance of the treated samples was improved by a factor of about 2.4 as compared to the as-received sample. It is also found that the sliding wear resistance can be further improved by surface alloying with TiN.