Synthesis and Characterization of Easily Colored Meta-aramid Copolymer Containing Ether Bonds
Synthesis and Characterization of Easily Colored Meta-aramid Copolymer Containing Ether Bonds作者机构：State Key Laboratory for Modification of Chemical Fibers and Polymer Materials College of Materials Science and Engineering Donghua University
出 版 物：《Chinese Journal of Polymer Science》 (高分子科学（英文版）)
年 卷 期：2019年第37卷第3期
页 面：227-234页
核心收录：
基 金：financially supported by the National Natural Science Foundation of China(No.51473031) the Shanghai International S&T Cooperation Fund(No.16160731302)
主 题：Copolymerized meta-aramid Solution polycondensation Dyeability
摘 要：This work described the preparation of easily colored meta-aramid(PMIA) copolymers from m-phenylenediamine(MPD),isophthaloyl dichloride(IPC), and 3,4′-oxydianiline(3,4′-ODA) via solution polycondensation in N,N-dimethylacetamide(DMAc). The novel co-PMIAs were obtained in relatively high inherent viscosities ranging from 1.32 dL/g to 2.53 dL/g, which could be easily cast into flexible films with high transparence or spun into fibers. All the newly synthesized copolymers possessed excellent thermal stabilities even better than that of commercial PMIA, with 5% weight loss temperatures higher than 430 °C in nitrogen measured by TGA and glass transition temperature of 267–277 °C measured by DSC. The cast films exhibited good mechanical properties with a tensile strength up to107 MPa and a tensile modulus up to 2.2 GPa. The resultant PMIAs also showed good solubility and better dye ability for cationic dyes.