Effect of Heat Treatment on Structure and Wear Resistance of High Chromium Cast Steel Containing Boron

作     者：Qi-hong CEN Hai-bin ZHANG Han-guang FU 

作者机构：School of Materials Science and EngineeringNational Engineering Research Center of Waste Resource RecoveryKunming University of Science and Technology School of Materials Science and EngineeringBeijing University of Technology 

出 版 物：《Journal of Iron and Steel Research International》 (国际钢铁研究杂志)

年 卷 期：2014年第21卷第5期

页      面：532-538页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

基　　金：Item Sponsored by National Natural Science Foundation of China(51274016) Natural Science Foundation of Beijing of China(2142009) Plan Item of Beijing Education Committee of China(KM201310005003) 

主　　题：high chromium cast steel boron alloying microstructure, mechanical property wear resistance 

摘      要：The microstructure, mechanical properties and wear resistance of high chromium cast steel containing boron after different heat treatments were studied by means of the optical microscopy （OM）, the scanning electron microscopy （SEM）, X-ray diffraction （XRD）, hardness, impact toughness, tensile and pin-on-disc abrasion tests. The results show that as cast microstructures of boron-free high chromium steel consist of martensite and a few （Cr, Fe）_7C_3 carbide, and the macro-hardness of boron-free high chromium steel is 55-57 HRC. After 0.5 mass% B was added into high chromium cast steel, as-cast structure transforms into eutectic （Fe, Cr）2B, （Cr, Fe）7 （C, B）a and martensite, and the macro-hardness reaches 58-60 HRC. High temperature quenching leads to the disconnection and isolated distribution of boride, and there are many （Cr,Fe）_23 （C,B）_6 precipitated phases in the quenching structure. Quenching from 1050 ℃, high chromium steel obtained the highest hardness, and the hardness of high chromium cast steel containing boron is higher than that of boron-free high chromium steel. The change of quenching temperature has no obvious effect on impact toughness of high chromium steel, and the increase of quenching temperature leads to tensile strength having an increasing tendency. At the same quenching temperature, the wear resistance of high chromium cast steel containing boron is more excellent than that of boron-free high chromium steel. High chromium cast steel guide containing boron has good performance while using in steel bar mill.