The Pore Structure of Phosphoaluminate Cement
The Pore Structure of Phosphoaluminate Cement作者机构：Guangdong Provincial Key Laboratory of Durability for Marine Civil Engineering Shenzhen University Shenzhen China School of Civil Engineering and Architecture Central South University Changsha China
出 版 物：《Open Journal of Composite Materials》 (复合材料期刊（英文）)
年 卷 期：2012年第2卷第3期
页 面：104-112页
主 题：Phosphoaluminate Cement Pore Structure Adsorption Curing Time
摘 要：The effects of curing time and water-to-cement ratio (W/C) on the pore structure of phosphoaluminate cement (PAC) paste are here presented. Based on the adsorption and condensation theory, the adsorption isotherm of hardened paste was tested using the Brunauer-Emmett-Teller (BET) nitrogen adsorption method. The phase composition and morphology of hydration products cured at different times were analyzed using X-ray diffraction (XRD), and a hydration heat test instrument (HHT) was employed to determine the heat of hydration. The effects of curing time and W/C on the pore structure of PAC are significant. The adsorption isotherm is fitted to the second category based on the Brun-auer- Deming-Deming-Teller (BDDT) classification system. Adsorption volume was found to increase with W/C and then decrease with age. The hysteresis loop of PAC is fitted to the H3 type based on International Union of Pure and Applied Chemistry (IUPAC) guidelines, and the adsorption volume and area enclosed by the hysteresis loop were found to increase with W/C and then decrease with age. BET surface and saturated adsorbed volume of PAC both increase with W/C and decrease with curing time, which is attributable to the greater hydration that produces and changes the characteristics of the pore structure.
维普期刊数据库