Composition and Refractory Properties of Mixtures of Moroccan Silica-Alumina Geomaterials and Alumina
Composition and Refractory Properties of Mixtures of Moroccan Silica-Alumina Geomaterials and Alumina作者机构：Department of Chemistry Faculty of Science and Technology University Hassan II Mohammedia Casablanca Morocco Department of Earth Sciences Geo-Materials and Geo-Environment Team (Geo M&E) Scientific Institute University Mohammed V Agdal Rabat Morocco
出 版 物：《New Journal of Glass and Ceramics》 (玻璃与陶瓷期刊（英文）)
年 卷 期：2013年第3卷第2期
页 面：59-66页
主 题：Clay Silica-Alumina Mullite Refractory Mechanical Properties
摘 要：Five mixtures (M1 to M5) of silica-alumina geomaterials and two varieties of alumina (AP and AR) were used for the elaboration of mullite refractory materials between 1500℃ and 1600℃. An X-ray diffraction (XRD) analysis showed that the refractory samples are composed of mullite, corundum and silica. The length of the mullite crystals was measured by a method of image analysis of scanning electron microscopy (SEM). Chemical and mechanical properties of these materials were investigated and correlated with their microstructure. Resistance towards Acid Attack test showed that the refractory samples present good resistance, as well as, the alumina powder AR obtained from waste of silica-alumina bricks proves to be efficient for an eventual use.
维普期刊数据库