Water leaching kinetics and recovery of potassium salt from sintering dust

作     者：詹光 郭占成 Guang ZHAN;Zhan-cheng GUO

作者机构：北京科技大学钢铁冶金新技术国家重点实验室北京100083 

出 版 物：《Transactions of Nonferrous Metals Society of China》 (中国有色金属学报（英文版）)

年 卷 期：2013年第23卷第12期

页      面：3770-3779页

核心收录：

学科分类：083002[工学-环境工程] 0830[工学-环境科学与工程（可授工学、理学、农学学位）] 08[工学] 

基　　金：Projects (2012AA062502 2012AA06A118) supported by the High-tech Research and Development Program of China 

主　　题：potassium salt sintering dust leaching kinetics intensified leaching 

摘      要：Surface morphology and inner structure of the dust were observed by ICP-AES, SEM-EDS and XRD to examine the strengthening measures of leaching potassium salt from the sintering dust by water. The results showed that the main component of the sintering dust was iron-oxygen compound, with KCl adsorbed on its surface. Leaching experiments showed that the KCl in the ESP dust could be separated and recovered by water leaching and fractional crystallization. The yield of K-Na vaporized crystalline salt was 18.56%, in which the mass fractions of KCl, NaCl, CaSO4 and K2SO4 were about 61.21%, 13.40%, 14.62%and 10.86%, respectively. The leaching kinetics of potassium salt from the sintering dust fits the external diffusion model well. The leaching speed and the leaching rate of the potassium salt can be increased by increasing the leaching temperature, strengthening the stirring speed and increasing the liquid-solid ratio.