The Mechanism of Ground Granulated Blastfurnace Slag Preventing Alkali Aggregate Reaction

作     者：STARK Jochen FREYBURG Ernst 

作者机构：F A Finger-Institute for Building Material Science of Bauhaus-University Weimar 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2010年第25卷第2期

页      面：332-341页

核心收录：

学科分类：080602[工学-钢铁冶金] 08[工学] 0806[工学-冶金工程] 

基　　金：Funded by the German Academic Exchange Service (DAAD) for the Project A/09/00743 the Science and Technology Project of Wuhan City(No.200860423208) 

主　　题：granulated blastfurnace slag (GBFS) alkali aggregate reaction (AAR) alkali content preventing mechanism 

摘      要：Three different methods were applied to study the alkali content of gelpores in cement. In the closed system, the concentration of K＋, Na＋ and OH - have not reduced with the increase of age. In the open system, the diffusion and transferring of K＋ and Na＋ towards free space leads to the de-crease of total alkali content. In the micro-analysis system, the contents of K＋ and Na＋ in the first hy- drated layer of ground granulated blastfurnace slag （GBFS） are very low, while the contents of calcium and magnesium are relatively high. This phenomenon shows that the mechanism of GBFS preventing alkali aggregate reaction （AAR） is： when GBFS is dissolved by alkali medium, SiO2 and Al2O3 are dissolved into the cement matrix, then around GBFS particles form reaction rings rich in Ca2＋ and Mg^2＋, and the C-S-H gel of positive charges formed in the area repulses K＋ and Na＋, which are forced to transfer to the mortar＇s matrix, pore or mortar sample surface. The transferred K ^＋ and Na^＋ form alkali gel products with other dissolved ions, then become evenly distributed in the mortar sample and react with Ca（OH）2 in pore solutions to form （Na,K）x-2z·zCa·（SiO2）y·（OH）x gel products; and thus changes the AAR gel products＇ structure. The gel products will not expand, and so they can delay expansion destruction.