Effect of ZnO-B_2O_3 Glass Addition on the Microwave Dielectric Properties of BaO-Nd_2O_3-TiO_2-Bi_2O_3 System

作     者：吴顺华 WU Shunhua, WEI Xuesong, WANG Shuang, GAO Shunqi (Institute of Electronic and Information Engineering, Tianjin University, Tianjin 300072, China)

作者机构：Institute of Electronic and Information Engineering Tianjin University 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2010年第25卷第5期

页      面：730-733页

核心收录：

学科分类：08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 080502[工学-材料学] 

基　　金：Funded by the Tianjin Natural Science Foundation of China (No.06YFJMJC01000) 

主　　题：BaO-Nd2O3-TiO2-Bi2O3 ZnO-B2O3 dielectric property sintering behavior 

摘      要：The effect of ZnO-B2O3（ZB） glass addition on the sintering behavior, microstructures and microwave dielectric properties of BaO-Nd2O3-TiO2-Bi2O3 （BNTB） system was investigated with the aid of X-ray diffraction, scanning electron microscopy and capacitance meter. It is found that the ZB glass addition, acting as a sintering aid, can effectively lower the sintering temperature of BNTB system to 850 ℃. The dielectric constant of BNTB-ZB ceramics increases with the increase of soaking time and the value of dielectric loss decreased with increasing soak time. The optical dielectric properties at 1 GHz of ε=74, tan δ=4×10^-4, and TCC=25 ppm/℃ were obtained for the BNTB system doped with 25 wt% ZB glass sintered at 850 ℃ for 2 h, representing that the BNTB-ZB ceramics could be promising for multilayer low temperature co-fired ceramics applications.