Gas adsorption in shaped zeolitic imidazolate framework-8

作     者：朱吉钦 江璐 代成娜 杨娜 雷志刚 

作者机构：State Key Laboratory of Chemical Resource EngineeringBeijing University of Chemical Technology 

出 版 物：《Chinese Journal of Chemical Engineering》 (中国化学工程学报（英文版）)

年 卷 期：2015年第23卷第8期

页      面：1275-1282页

核心收录：

学科分类：081704[工学-应用化学] 07[理学] 070304[理学-物理化学(含∶化学物理)] 08[工学] 0817[工学-化学工程与技术] 0703[理学-化学] 

基　　金：Supported by the National Natural Science Foundation of China(21176010 21476009 21406007 and U1462104) 

主　　题：ZIF 8 Shaping Gas adsorption Model reduction Materials 

摘      要：Zeolitic imidazolate framework-8(ZIF-8) was prepared through a solve-thermal reaction method and then shaped using different additives. The in fluence of the shaping conditions on the microstructure of the shaped samples was characterized by the XRD, BET, and SEM techniques. The results demonstrate that the compressive strength of the various shaped tablets is greatly increased and capable of meeting the industrial requirements compared to the unshaped ZIF-8 and that the loss rate of speci fic surface areas was maintained at 10% after the addition of 10%(by mass) binder and 10%(by mass) solvent. The adsorption isotherms of CO2, CH4, C3H8, and C3H6 on powdery ZIF-8and the shaped tablets(T-shaped ZIF-8, C-shaped ZIF-8, and N-shaped ZIF-8) were determined through volumetric measurements under different pressures and temperatures(298.2, 323.2, and 348.2 K). The adsorption capacities of the gases on both the ZIF-8 powder and the shaped tablets follow the order C3H6 N C3H8N CO2 N CH4. Furthermore,the results show that the adsorption capacities of the gases on the shaped tablets are lower by approximately 10%–20% than those on the powdery ZIF-8. In fact, the adsorption equilibrium isotherms for CO2, CH4, C3H8, and C3H6 on both powdery and shaped ZIF-8 can be well described by the Langmuir equation.