Photoluminescent Properties of New Phosphor Sr_2ZnSi_2O_7:M(M=Mn^(2+), Tb^(3+))

作     者：郝艳 

作者机构：State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials Southwest University of Science and Technology 

出 版 物：《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报（材料科学英文版）)

年 卷 期：2015年第30卷第1期

页      面：97-99页

核心收录：

学科分类：081702[工学-化学工艺] 08[工学] 0817[工学-化学工程与技术] 

基　　金：Funded by Key Project of Natural Science for Education Department of Sichuan Province(No.14ZA0102) State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials,Southwest University of Science and Technology,Mianyang 

主　　题：Sr2ZnSi2O7: Mn2+, Tb3+ phosphor UV VUV 

摘      要：New phosphors Sr2ZnSi2O7： M （M=Mn2＋, Tb3＋） were synthesized through solid-state reaction, and their photoluminescent properties under UV and VUV region were investigated. The results showed that Sr2ZnSi2O7：Mn2＋ emitted green light with the strongest emission peak centered at 525 nm, and its quenching concentration under 254 and 147 nm excitation occurred at x = 0.08 and 0.06, respectively. Sr2ZnSi2O7： Th3＋ emitted green light with the strongest emission peak centered at 541 nm, and its quenching concentration under 254 and 147 nm excitation also appeared at y = 0.25. At 147 nm excitation, the emission intensities of Sr2Zn0.54Si2O7： 0.06Mn2＋ and Sr1.75ZnSi2O7： 0.25Tb3＋ phosphors were 54% and 36% of that of Zn1.96SiO4：0.04Mn2＋, respectively. And their decay times （τ1/e） were about 3.18 ms and 3.9 ms, respectively.