BaWO_4纳米线束的合成及其光学性质研究(英文)
Scheelite BaWO_4 Nanowire Bundles:Controllable Synthesis and Optical Properties作者机构:南京大学化学化工学院配位化学国家重点实验室 江苏大学化学化工学院镇江212013
出 版 物:《无机化学学报》 (Chinese Journal of Inorganic Chemistry)
年 卷 期:2007年第23卷第10期
页 面:1796-1800页
核心收录:
学科分类:081704[工学-应用化学] 07[理学] 08[工学] 0817[工学-化学工程与技术] 0703[理学-化学] 070301[理学-无机化学]
基 金:国家自然科学基金资助项目(No.90606005 20490210)
摘 要:High quality BaWO4 nanowire bundles have been synthesized in toluene-sodium dodecylbenzene sulphonate (SDBS)-small amount PEG20000-H2O reverse micelle system. XRD result shows that the obtained BaWO4 belongs to tetragonal phase with scheelite structure. TEM results demonstrate that the obtained BaWO4 nanowire bundles have high aspect-ratio (650). The experimental results confirm that PEG20000 plays a key role for the formation of BaWO4 nanowire bundles. Other factors which influence the morphology and crystallinity of the product are also briefly discussed. Moreover, the obtained BaWO4 nanowire bundles exhibit strong photoluminescence centered at 397.3 nm with λex=343.5 nm at room temperature, which is different from the bulk BaWO4 crystals.