Preparation and properties of nano-composite ceramic coating by thermo chemical reaction method
Preparation and properties of nano-composite ceramic coating by thermo chemical reaction method作者机构:Dept.of MaterialLiaoning Technical UniversityFuxin 123000China
出 版 物:《Journal of Coal Science & Engineering(China)》 (煤炭学报(英文版))
年 卷 期:2007年第13卷第2期
页 面:211-214页
学科分类:080503[工学-材料加工工程] 0808[工学-电气工程] 08[工学] 0818[工学-地质资源与地质工程] 0807[工学-动力工程及工程热物理] 0815[工学-水利工程] 0805[工学-材料科学与工程(可授工学、理学学位)] 0813[工学-建筑学] 0814[工学-土木工程]
基 金:Liaoning Nature Fund Item(20062203)
主 题:thermo chemical reaction nano-composite ceramic coating bonding strength corrosion resistance abrasion resistance
摘 要:Nano-composite ceramic coating was fabricated on Q235 steel through thermo chemical reaction method. Structure of the coating was analyzed and the properties were tested. The results show that a few of new ceramic phases, such as MgAI2O4, ZnAI2O4, AI2SiO5, Ni3Fe and Fe3AI, are formed on the coating during the process of solidifying at 600 ℃. The ceramic coating is dense and the high bonding strength is obtained. The average bonding strength between the coating and matrix could be 14.22 MPa. The acid resistance of the coating increase by 8.8 times, the alkali resistance by 4.1 times, the salt resistance bv 10.3 times, and the wear resistance bv 2.39 times.