EFFECT OF SLIP ORIENTATION ON STRESS RESPONSE,INTERNAL FRICTION AND ULTRASONIC ATTENUATION DURING CYCLIC DEFORMATION IN Al SINGLE CRYSTALS
EFFECT OF SLIP ORIENTATION ON STRESS RESPONSE,INTERNAL FRICTION AND ULTRASONIC ATTENUATION DURING CYCLIC DEFORMATION IN Al SINGLE CRYSTALS作者机构:Inst of Metal Research Acad Sinica Shenyang China
出 版 物:《Acta Metallurgica Sinica(English Letters)》 (金属学报(英文版))
年 卷 期:1992年第5卷第6期
页 面:471-476页
核心收录:
学科分类:0810[工学-信息与通信工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0812[工学-计算机科学与技术(可授工学、理学学位)]
主 题:crystal orientation cyclic deformation stress response internal friction ultrasonic attenuation Al
摘 要:The variation of cyclic stress,internal friction and ultrasonic attenuation during cyclic deformation and relations among them have been investigated with different slip orientation Al single *** results indicate that the value of cyclic stress σ,internal friction Q^(-1)and ultrasonic attenuation △α depend obviously on the slip *** are large differences in above three parameters for different slip orientation Al *** early stage of fatigue life,σ and △α increase and Q^(-1)decreases with cycles N,and △α reached maxi- mum before σ,while Q^(-1)and σ get the valley and the peak,respectively,at same cycles.