C02 adsorption performance of ZIF-7 and its endurance in flue gas components
C02 adsorption performance of ZIF-7 and its endurance in flue gas components作者机构:School of Environmental Science and Engineering Shanghai Jiao Tong University Shanghai 200240 China
出 版 物:《Frontiers of Environmental Science & Engineering》 (环境科学与工程前沿(英文))
年 卷 期:2014年第8卷第2期
页 面:162-168页
核心收录:
学科分类:081702[工学-化学工艺] 08[工学] 0817[工学-化学工程与技术] 0822[工学-轻工技术与工程]
主 题:ZIF-7 structural stability CO2 capture ther- mal stability
摘 要:Porous ZIF-7 with the sodalite (SOD) cage structure (ZIF, Zeolitic imidazolate framework) were synthesized by the solvothermal method. Synthesized material was characterized by powder X-ray diffraction (PXRD), thermal gravity (TG), scanning electron micro- scopy (SEM) and Na adsorption analysis. ZIF-8 with the SOD structure and a littl larger pore window was synthesized in a similar way and was characterized for comparisons. Thermal stability and structural stability of ZIF-7 were tested through PXRD analysis, and the capability of the material for CO2 capture from simulated flue gas was investigated through physical adsorption method. The results showed that CO: adsorption capacity on ZIF-7 was about 48 mL. gl while the capacity on ZIF-8 was about 18mg.g-1 (at 12C and 0.98 P/Po relative pressure). Furthermore, the impact of flue gas components on adsorption capacity of ZIF-7 and the selectivity of CO2 against N2 on ZIF-7 was also investigated in this work