Effect of substrate curvature on thickness distribution of polydimethylsiloxane thin film in spin coating process

作     者：Ying Yan Ping Zhou Shang-Xiong Zhang Xiao-Guang Guo Dong-Ming Guo 闫英;周平;张尚雄;郭晓光;郭东明

作者机构：Key Laboratory for Precision and Non-traditional Machining Technology of Ministry of Education Dalian University of Technology Dalian 116024 China 

出 版 物：《Chinese Physics B》 (中国物理B（英文版）)

年 卷 期：2018年第27卷第6期

页      面：479-487页

核心收录：

学科分类：07[理学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0704[理学-天文学] 0702[理学-物理学] 

基　　金：supported by the National Natural Science Foundation of China(Grant Nos.51605079 and 51475076) the Science Fund for Creative Research Groups of the National Natural Science Foundation of China(Grant No.51621064) the China Postdoctoral Science Foundation(Grant No.2016M591424) 

主　　题：spin coating non-planar substrate film thickness distribution edge-bead effect 

摘      要：The polymer spin coating is critical in flexible electronic manufaction and micro-electro-mechanical system（MEMS）devices due to its simple operation, and uniformly coated layers. Some researchers focus on the effects of spin coating parameters such as wafer rotating speed, the viscosity of the coating liquid and solvent evaporation on final film *** this work, the influence of substrate curvature on film thickness distribution is considered. A new parameter which represents the edge bead effect ratio（re） is proposed to investigate the influence factor of edge bead effect. Several operation parameters including the curvature of the substrate and the wafer-spin speed are taken into account to study the effects on the film thickness uniformity and edge-bead ratio. The morphologies and film thickness values of the spin-coated PDMS films under various substrate curvatures and coating speeds are measured with laser confocal microscopy. According to the results, both the convex and concave substrate will help to reduce the edge-bead effect significantly and thin film with better surface morphology can be obtained at high spin speed. Additionally, the relationship between the edge-bead ratio and the thin film thickness is like parabolic curve instead of linear dependence. This work may contribute to the mass production of flexible electronic devices.