Microstructure and mechanical properties of Al/Cu/Mg laminated composite sheets produced by the ARB proces
Microstructure and mechanical properties of Al/Cu/Mg laminated composite sheets produced by the ARB proces作者机构:School of Mechanical EngineeringIran University of Science and Technology Department of Materials EngineeringSahand University of Technology School of Mechanical EngineeringCollege of EngineeringUniversity of Tehran
出 版 物:《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报(英文版))
年 卷 期:2018年第25卷第5期
页 面:564-572页
核心收录:
学科分类:0709[理学-地质学] 0819[工学-矿业工程] 0806[工学-冶金工程] 08[工学] 0708[理学-地球物理学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
主 题:multi-layered composite Al/Cu/Mg accumulative roll bonding fractography mechanical properties microstructure
摘 要:In the present study, an Al/Cu/Mg multi-layered composite was produced by accumulative roll bonding(ARB) through seven passes, and its microstructure and mechanical properties were evaluated. The microstructure investigations show that plastic instability occurred in both the copper and magnesium reinforcements in the primary sandwich. In addition, a composite with a perfectly uniform distribution of copper and magnesium reinforcing layers was produced during the last pass. By increasing the number of ARB cycles, the microhardness of the layers including aluminum, copper, and magnesium was significantly increased. The ultimate tensile strength of the sandwich was enhanced continually and reached a maximum value of 355.5 MPa. This strength value was about 3.2, 2, and 2.1 times higher than the initial strength values for the aluminum, copper, and magnesium sheets, respectively. Investigation of tensile fracture surfaces during the ARB process indicated that the fracture mechanism changed to shear ductile at the seventh pass.