Microstructure and mechanical properties of SiC-particle-strengthening tri-metal Al/Cu/Ni composite produced by accumulative roll bonding process

作     者：Moslem Tayyebi Beitallah Eghbali 

作者机构：Department of Material Engineering Sahand University of Technology 

出 版 物：《International Journal of Minerals,Metallurgy and Materials》 (矿物冶金与材料学报（英文版）)

年 卷 期：2018年第25卷第3期

页      面：357-364页

核心收录：

学科分类：0709[理学-地质学] 0819[工学-矿业工程] 08[工学] 0806[工学-冶金工程] 0708[理学-地球物理学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学（可授工学、理学学位）] 0702[理学-物理学] 

主　　题：accumulative roll bonding Al/Ni/Cu/SiC composite silicon carbide particles microstructure mechanical properties 

摘      要：In this study, a multilayer Al/Ni/Cu composite reinforced with Si C particles was produced using an accumulative roll bonding(ARB) process with different cycles. The microstructure and mechanical properties of this composite were investigated using optical and scanning microscopy and hardness and tensile testing. The results show that by increasing the applied strain, the Al/Ni/Cu multilayer composite converted from layer features to near a particle-strengthening characteristic. After the fifth ARB cycle, a composite with a uniform distribution of reinforcements(Cu, Ni, and SiC) was fabricated. The tensile strength of the composite increased from the initial sandwich structure to the first ARB cycle and then decreased from the first to the third ARB cycle. Upon reaching five ARB cycles, the tensile strength of the composite increased again. The variation in the elongation of the composite exhibited a tendency similar to that of its tensile strength. It is observed that with increasing strain, the microhardness values of the Al, Cu, and Ni layers increased, and that the dominant fracture mechanisms of Al and Cu were dimple formation and ductile fracture. In contrast, brittle fracture in specific plains was the main characteristic of Ni fractures.