Influences of substrate temperature on microstructure and corrosion behavior of APS Ni_(50)Ti_(25)Al_(25) inter-metallic coating
Influences of substrate temperature on microstructure and corrosion behavior of APS Ni_(50)Ti_(25)Al_(25) inter-metallic coating作者机构:Plasma Physics Research Center Science and Research Branch Islamic Azad University Department of Materials Engineering Science and Research Branch Islamic Azad University
出 版 物:《Chinese Physics B》 (中国物理B(英文版))
年 卷 期:2018年第27卷第2期
页 面:607-612页
核心收录:
学科分类:080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0704[理学-天文学]
主 题:Ni50Ti25Al25 coating air plasma spray planetary ball milling inter metallic compounds corrosion resistance
摘 要:In the present investigation, Ni_(50)Ti_(25)Al_(25)(at.%) mechanically alloyed powder is deposited on carbon steel *** the coating process, the substrate is heated to temperature ranging from room temperature to 400℃. The microstructure, porosity, microhardness, adhesion strength, and corrosion behavior of the coating are investigated at different substrate temperatures. Results show that coating porosity is lower on high temperature surface. Microhardness and adhesion strength of the deposition layer on the substrate without preheating have lower values than with preheating. The polarization test result shows that corrosion performance of the coating is dependent on micro cracks and porosities and the increasing of substrate temperature can improve the quality of coating and corrosion performance.