Deep drawing of aluminum alloy 7075 using hot stamping

作     者：Wen-Chao Xiao Bao-Yu Wang Yi Kang Wei-Ping Ma Xue-Feng Tang 

作者机构：School of Mechanical Engineering University of Science and Technology Beijing Beijing 100083 China 

出 版 物：《Rare Metals》 (稀有金属（英文版）)

年 卷 期：2017年第36卷第6期

页      面：485-493页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

基　　金：financially supported by the National Natural Science Foundation of China (No.U1564202) 

主　　题：Aluminum alloy 7075 Aluminum hotstamping Process parameters Formability Mechanicalproperty 

摘      要：In this paper, simulations of deep drawing tests at elevated temperatures were carried out with experimental validation. The aim of this work was to study the effect of process parameters on formability and mechanical properties of aluminum alloy 7075 in hot stamping *** parameters, including blank temperature, stamping speed, blank holder force and friction coefficient, were studied. Stamping tests were conducted at temperatures between 350 and 500 ℃, blank holder force between 0 and 10 kN, stamping speed between 50 and 150 mm·s^-1, and friction coefficient between 0.1 and 0.3. Based on the analysis, it is shown that thickness homogeneity could be improved when the blank is formed at lower temperature,lower blank holder force and lower friction *** could be improved when the blank was well lubricated at about 400 ℃. Formability at stamping speed 50 mm·s^-1 is far better than those at other speeds. The mechanical property analysis shows that the hot stamping process could make the formed part to obtain high quality.