W-Mo-Si/SiC Oxidation Protective Coating for Carbon/Carbon Composites
W-Mo-Si/SiC Oxidation Protective Coating for Carbon/Carbon Composites作者机构:National Key Laboratory of Thermostructure Composite Materials Northwestern Polytechnical University Xi'an 710072 China
出 版 物:《Journal of Materials Science & Technology》 (材料科学技术(英文版))
年 卷 期:2007年第23卷第4期
页 面:559-562页
核心收录:
学科分类:081702[工学-化学工艺] 0817[工学-化学工程与技术] 0806[工学-冶金工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
基 金:国家重点基础研究发展计划(973计划) 航天科技基金
主 题:C/C composites Coating Microstructure Oxidation
摘 要:A W-Mo-Si/SiC double-layer oxidation protective coating for carbon/carbon (C/C) composites was prepared by a two-step pack cementation technique. XRD (X-ray diffraction) and SEM (scanning electron microscopy)results show that the coating obtained by the first step pack cementation was a thin inner buffer layer of SiC with some cracks and pores, and a new phase of (WxMo1-x)Si2 appeared after the second step pack cementation. Oxidation test shows that, after oxidation in air at 1773 K for 175 h and thermal cycling between 1773 K and room temperature for 18 times, the weight loss of the W-Mo-Si/SiC coated C/C composites was only 2.06%. The oxidation protective failure of the W-Mo-Si/SiC coating was attributed to the formation of some penetrable cracks in the coating.