Effect of Nano Clay on Corrosion Protection of Zinc-rich Epoxy Coatings on Steel 37作者机构:Abadan Faculty of Petroleum Engineering Petroleum University of Technology Technical Faculty South Tehran Branch Islamic Azad University
出 版 物:《Journal of Materials Science & Technology》 (材料科学技术(英文版))
年 卷 期:2016年第32卷第11期
页 面:1152-1160页
核心收录:
学科分类:080503[工学-材料加工工程] 0817[工学-化学工程与技术] 0806[工学-冶金工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学] 0802[工学-机械工程] 0801[工学-力学(可授工学、理学学位)] 0702[理学-物理学]
主 题:Epoxy coatings Zinc rich Impedance Cathodic protection Clay
摘 要:Epoxy zinc rich coatings containing clay nanoparticles were prepared and the effect of clay content on the cathodic protection performance of the coatings was evaluated by electrochemical impedance spectroscopy(EIS) and immersion test. Open circuit potential(OCP) measurements and immersion tests were also carried out to better understand the behavior of zinc rich coating. EIS and OCP measurements showed that addition of 1 wt% clay improved the cathodic protection duration and sacrificial properties of the epoxy zinc rich coating. Transmission electron microscopy(TEM) photographs confirmed that clay nanoparticles were successfully dispersed in the coating matrix loaded with 1 wt% clay. Immersion test results indicated that addition of 1 wt% clay nanoparticles in zinc rich epoxy coatings increased the cathodic protection ability of coatings.