Corrosion behavior of hypoeutectic Al-Cu alloys in H_2SO_4 and NaCl solutions

作     者：Wislei R.Osório Leandro C.Peixoto Leonardo R.Garcia Amauri Garcia 

作者机构：Department of Materials EngineeringUniversity of Campinas-UNICAMP 

出 版 物：《Acta Metallurgica Sinica(English Letters)》 (金属学报（英文版）)

年 卷 期：2009年第22卷第4期

页      面：241-246页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

主　　题：Al-Cu alloys Al2Cu Corrosion Microstructure Castings 

摘      要：The aim of this work was to evaluate the electrochemical behaviour of hypoeutectic Al-Cu alloys immersed in two different solutions containing sulphate and chloride ions, respectively. The influence of Al2Cu associated to the dendritic arm spacing on the general corrosion resistance of such alloys is analysed. The typical microstructural pattern was examined by using scanning electron microscope. The corrosion tests were performed in both 0.5 M sulphuric acid and 0.5 M NaCl solutions at 25℃ by using an electrochemical impedance spectroscopy （EIS） technique and potentiodynamic polarization curves. Equivalent circuits by using the ZView software, were also used to provide quantitative support for the discussions. It was found that as the Cu content increased （i.e., increasing the Al2Cu fraction）, a higher susceptibility to the corrosion action in the NaCl solution is detected. In contrast, the tests carried out in the H2SO4 solution resulted in similar corrosion,rates for the three different hypoeutectic alloys.