Removal of reactive bright-red X-3B in water by Ti/13X molecular sieves
Removal of reactive bright-red X-3B in water by Ti/13X molecular sieves作者机构：College of Urban Construction and Environment Engineering University of Shanghai for Science and Technology Shanghai 200093 China
出 版 物：《Journal of Environmental Science and Engineering》 (环境科学与工程（英文版）)
年 卷 期：2008年第2卷第1期
页 面：13-17,35页
学科分类：083002[工学-环境工程] 0830[工学-环境科学与工程（可授工学、理学、农学学位）] 081702[工学-化学工艺] 08[工学] 0817[工学-化学工程与技术]
主 题：microporous molecular sieves TiO2 photocatalysis dyes
摘 要：The compound materials （shorted by Ti/13X） of doping of TiO2 into 13X molecular sieves has-been achieved by methods namely impregnation. Technical parameters of preparation for Ti/13X were determined by removal efficiency of simulation dyeing wastewater containing reactive bright-red X-3B （shorted by X-3B）. In various preparation parameters, the influence of Ti loaded on 13X molecular sieves on X-3B removal efficiency is most important. The optimum condition for volume of TiCI4 loaded on 13X molecular sieves is 8 ml at 95.9%, produced sample referred as M8. M8 was characterized using X-Ray Diffraction （XRD）, Scanning Electron Microscope （SEM）. XRD patterns of M8 revealed the incorporation of titanium into framework of 13X molecular sieves, due to the presence ofTiO2 anatase phase. SEM image showed that M8 has a large number of wormhole-like channels, in comparison with that of 13X molecular sieves. The photocatalytic tests were carried out for degradation of X-3B. The results showed that the dosage of Ti/13X, reaction time, pH, and concentration of X-3B influence the X-3B removal efficiency. The optimum conditions of photodegradation as the following： MS/X-3B ratio, Conc. is 0.3 g/l, reaction time is 120 rain, pH is 2-6. The photodegradation reaction of Ti/13X with X-3B followed first order kinetics. The rate constants and t1/2 for M8 sample at 0.3 g/l M8/ X-3B solution ratio were 430 min^-1 and 16 min, respectively.
维普期刊数据库