Effect of Isothermal Annealing on Nano Ti-Carbides Precipitation

作     者：Cheol-ho Park Woo-jin Kim Nam-hyun Kang Hyung-hyup Do Kyung-Mox Cho 

作者机构：Department of Materials Science and EngineeringPusan National UniversityBusan 609-735Korea Technical Research LaboratoriesHyundai steelsDangjinChungnam 343-711Korea 

出 版 物：《Journal of Iron and Steel Research International》 (钢铁研究学报(英文版))

年 卷 期：2011年第18卷第S1期

页      面：287-289页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0802[工学-机械工程] 080201[工学-机械制造及其自动化] 

主　　题：Ti carbide hot rolled steel hole expansion ratio isothermal holding nano precipitates 

摘      要：Transmission electron microscopy was used to investigate the effect of isothermal holding temperature and time on the nano Ti-precipitates.A holding temperature was varied systematically from 400℃ to 1200℃.The isothermal holding was continued for 30s,300s and 900s,*** carbides of (Ti,Nb)C were precipitated significantly at 900℃.The size of carbides was approximately 10nm at 30s holding and increased to 20～30nm at 900s *** holding at 1000℃ showed the increased amount of carbides larger than *** 800℃,nano (Ti,Nb)C was not observed at 30s and it was examined at *** size of nano (Ti,Nb)C was smaller than that of 900℃.As the isothermal temperature decreased to 700 ℃,the nano (Ti,Nb)C was only seen at 900s holding and the size of carbides was smaller than *** (Ti,Nb)C was disappeared at isothermal holding below 600℃.The kinetics of nano (Ti,Nb)C precipitation were studied as a function of isothermal holding temperature and time,respectively,using the precipitate growth equations.