Morphology and electrical contact properties of electrical connection materials in corrosive atmosphere

作     者：Zhi-Gang Kong Liang-Jun Xu 

作者机构：Research Laboratory of Electrical ContactsBeijing University of Posts and Telecommunications 

出 版 物：《Rare Metals》 (稀有金属（英文版）)

年 卷 期：2013年第32卷第2期

页      面：174-178页

核心收录：

学科分类：080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 

基　　金：supported by the Chinese Universities Scientific Fund(No.2011RC0603) 

主　　题：Electrical contact Porosity Corrosion Temperature 

摘      要：The impact mechanism of environmental fac tors, such as corrosive atmosphere, on connector materials was investigated, and the porosity of gold plating was tested. Series of inspections and analytical research meth ods were introduced in this article. The surface morphology of specimens after corrosion was observed by stereoscopic microscope and scanning electron microscope. Chemical constitution was examined by Xray energy spectrum. The contact resistances were measured by fourpoint method. The experiment results show that after exposure to certain environment, the corrosion products, such as Cu20, Cu（NO3）2.3H20, and NiO, are observed on the surface of the specimens without gold coatings, whereas the corrosion products appear to have circleshaped spots on goldplating surface after corrosion test, which indicate that the gold plating has good corrosion protection. The porosity is increased with the increase of corrosion time for every kind of specimens gold plated, and the corrosion degree of gold plating specimens is decreased with the increase of the thickness of gold coatings. The static contact resistances of circleshaped spots appear higher contact resistance than normal value, which can reach to 2,000 mr2 nearly. It is found that the high and unstable contact resistance of the pore and products is more likely to cause contact failure.