Preparation and Microstructure of Glass-ceramics and Ceramic Composite Materials
Preparation and Microstructure of Glass-ceramics and Ceramic Composite Materials作者机构:School of Materials Science and Engineering Wuhan University of Technology Wuhan 430070 China
出 版 物:《Journal of Wuhan University of Technology(Materials Science)》 (武汉理工大学学报(材料科学英文版))
年 卷 期:2008年第23卷第4期
页 面:562-565页
核心收录:
学科分类:081704[工学-应用化学] 07[理学] 08[工学] 0817[工学-化学工程与技术] 070305[理学-高分子化学与物理] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0703[理学-化学] 0702[理学-物理学]
基 金:the National Supporting Plan of China(No. 2006BAJ02B03)
主 题:CaO-Al2O3-SiO2 system glass-ceramic ceramic body
摘 要:The technology and microstructure of glass-ceramics and ceramic composite materials were studied. A suitable ceramic body was chosen on the basis of the sintering temperature of CaO-Al2O3-SiO2 system glass-ceramics. According to the expansion coefficient of the ceramic body, that of CaO-Al2O3-SiO2 system glass-ceramics was adjusted, fl-wollastonite was found present as the major crystalline phase in glass- ceramic. The CaO-Al2O3-SiO2 system glass-ceramic layer and ceramic body could be sintered together by adjusting the sintering period. The compositions of glass-ceramic layer and ceramic body diffuse mutually at 1 100 ℃, resulting in an interface between them. To achieve good sintered properties of glass-ceramics and the chosen ceramic body, at least a four-hour sintering time is used.