Effect of V content on microstructures and properties of TiC cermet fusion welding interface
作者机构:Zhengzhou Research Institute of Mechanical Engineering Co.Ltd.Zhengzhou 450001China Zhengzhou UniversityZhengzhou 450001China
出 版 物:《China Welding》 (中国焊接(英文版))
年 卷 期:2024年第33卷第1期
页 面:40-45页
学科分类:080503[工学-材料加工工程] 08[工学] 0805[工学-材料科学与工程(可授工学、理学学位)] 0802[工学-机械工程] 080201[工学-机械制造及其自动化]
主 题:TiC cermet MIG welding interface V content shear strength
摘 要:The effects of vanadium(V)on the microstructures and mechanical properties of the TiC cermet fusion welding interface were studied by adjusting the content of V in the self-developed flux-cored wires using metal inert gas arc(MIG)welding for surfacing on the TiC *** results show that the increase in V content promotes the element diffusion between TiC cermet and weld *** are no de-fects observed in the interface,and the diffusion of elements refers to excellent metallurgical *** shear strength of the fusion zone initially decreases and then increases with the increase in V *** maximum shear strength of the TiC cermet/weld interface,reaching 552 MPa,occurred when the V content reached 0.65%.Meanwhile,the average hardness in the transition zone reached 488.2 HV0.2.