Construction of a High‑Performance Composite Solid Electrolyte Through In‑Situ Polymerization within a Self‑Supported Porous Garnet Framework

作     者：An‑Giang Nguyen Min‑Ho Lee Jaekook Kim Chan‑Jin Park An-Giang Nguyen;Min-Ho Lee;Jaekook Kim;Chan-Jin Park

作者机构：Department of Materials Science and EngineeringChonnam National University77 Yongbong‑roBuk‑guGwangju 61186South Korea 

出 版 物：《Nano-Micro Letters》 (纳微快报（英文版）)

年 卷 期：2024年第16卷第5期

页      面：56-70页

核心收录：

学科分类：0808[工学-电气工程] 08[工学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0702[理学-物理学] 

基　　金：supported by the National Research Foundation of Korea (NRF) grant funded by the MSIT,Korea (No. 2018R1A5A1025224 and No. 2019R1A2C1084020) this research received funding support from a grant from the Korea Planning&Evaluation Institute of Industrial Technology (KEIT),funded by the MOTIE of Korea (No. 10077287)。 

主　　题：Scalable tape-casting method Self-supported porous Li_(6.4)La_(3)Zr_(1.4)Ta_(0.6)O_(12) Composite solid electrolyte LiF-and B-rich interphase layers 

摘      要：Composite solid electrolytes(CSEs)have emerged as promising candidates for safe and high-energy–density solid-state lithium metal batteries(SSLMBs).However,concurrently achieving exceptional ionic conductivity and interface compatibility between the electrolyte and electrode presents a significant challenge in the development of high-performance CSEs for SSLMBs.To overcome these challenges,we present a method involving the in-situ polymerization of a monomer within a self-supported porous Li_(6.4)La_(3)Zr_(1.4)Ta_(0.6)O_(12)(LLZT)to produce the CSE.The synergy of the continuous conductive LLZT network,well-organized polymer,and their interface can enhance the ionic conductivity of the CSE at room temperature.Furthermore,the in-situ polymerization process can also con-struct the integration and compatibility of the solid electrolyte–solid electrode interface.The synthesized CSE exhibited a high ionic conductivity of 1.117 mS cm^(-1),a significant lithium transference number of 0.627,and exhibited electrochemical stability up to 5.06 V vs.Li/Li+at 30℃.Moreover,the Li|CSE|LiNi_(0.8)Co_(0.1)Mn_(0.1)O_(2) cell delivered a discharge capacity of 105.1 mAh g^(-1) after 400 cycles at 0.5 C and 30℃,corresponding to a capacity retention of 61%.This methodology could be extended to a variety of ceramic,polymer electrolytes,or battery systems,thereby offering a viable strategy to improve the electrochemical properties of CSEs for high-energy–density SSLMBs.