Structure regulating of metal clusters in carbonized metallic organic frameworks for high-efficient microwave absorption via tuning interaction strength between metals and ligands
作者机构：School of Chemistry and Chemical EngineeringChongqing Key Laboratory of Soft-Matter Material Chemistry and Function ManufacturingSouthwest UniversityChongqing 400715China Jieyang Branch of Chemistry and Chemical Engineering Guangdong Laboratory(Rongjiang Laboratory)Jieyang 515200China
出 版 物：《Nano Research》 (纳米研究（英文版）)
年 卷 期：2024年第17卷第3期
页 面：1699-1709页
核心收录：
学科分类：07[理学] 070304[理学-物理化学(含∶化学物理)] 0805[工学-材料科学与工程（可授工学、理学学位）] 0703[理学-化学] 0702[理学-物理学]
基 金：We thank the National Natural Science Foundation of China(No.52173264)for financial support。
主 题：heterogeneous interface carbonized metallic organic frameworks microwave absorption interfacial polarization
摘 要：Carbonized metallic organic frameworks(CMOF)have been attracting attention in microwave absorption(MA)research area because of their diverse structures,tunable compositions,and rich porosity.Herein,structure regulation on metal clusters in CMOF is achieved by tuning the interaction strength between metals and ligands to enhance microwave absorption performance.Due to relatively weak interaction among copper cations and ligands,copper nanoclusters(CuNC)can be uniformly formed and embedded within the cobalt/zinc(Co/Zn)CMOF.Firstly,copper cations are added to the Co/Zn bimetallic zeolitic imidazolate frameworks(ZIFs).Secondly,the CMOF composite particles with CuNCs(CuNCs/CoZn-CMOF)were developed by a pyrolysis process.The CuNCs/CoZn-CMOF with an appropriate amount of CuNCs can harmonize both dielectric and magnetic losses.As a result,the minimum reflection loss(RLmin)reaches–45.1 dB at a matching thickness of 2.30 mm and the effective absorption bandwidth(EAB)is 8.80 GHz at a thickness of 3.10 mm.The broadband response to electromagnetic waves is attributed to interfacial polarization at CuNCs surface and heterogeneous interfaces,impedance matching and multiple scattering of electromagnetic waves.This study provides a feasible method to develop CMOF microwave absorption materials with high EAB values.