Effect of CaO/Al_(2)O_(3)on structure,viscosity,and surface tension of electroslag remelting-type CeO_(2)-bearing slag
作者机构：Hubei Provincial Key Laboratory for New Processes of Ironmaking and SteelmakingWuhan University of Science and TechnologyWuhan 430081HubeiChina The State Key Laboratory of Refractories and MetallurgyWuhan University of Science and TechnologyWuhan 430081HubeiChina Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of EducationWuhan University of Science and TechnologyWuhan 430081HubeiChina
出 版 物：《Journal of Iron and Steel Research(International)》 (钢铁研究学报（英文版）)
年 卷 期：2023年第30卷第4期
页 面：717-725页
核心收录：
学科分类：080602[工学-钢铁冶金] 08[工学] 0806[工学-冶金工程] 0703[理学-化学]
基 金：the National Natural Science Foundation of China(Grant No.52104339) the Hubei Provincial Key Laboratory for New Processes of Ironmaking and Steelmaking(Grant No.KF-20-3)is greatly acknowledged.
主 题：Electroslag remelting CeO_(2)-bearing slag CaO/Al_(2)O_(3) Structure Viscosity Surface tension
摘 要：The structure of electroslag remelting-type CaF_(2)–CaO–Al_(2)O_(3)–CeO_(2)slag with various CaO/Al_(2)O_(3)mass ratios and its correlation with viscosity and surface tension were investigated.The Raman analysis of the slag shows that with increasing CaO/Al_(2)O_(3)mass ratio from 0.70 to 1.29 in the slag,the polymerization degree of the slag decreased,which was because more complex[AlO_(4)]-tetrahedral units of Q_(Al)^(3) and Q_(Al)^(4)were depolymerized to form relatively simpler structural units Q_(Al)^(0),Q_(Al)^(1),and Q_(Al)^(2),and the excess oxygen ions introduced by CaO promoted the transformation of[AlO_(4)]-tetrahedral units to[AlO_(6)]-octahedral units.Increasing CaO/Al_(2)O_(3)mass ratio has an obvious effect on reducing the viscosity and activation energy for viscous flow of the slag,resulting from the depolymerization of the slag.Owing to the decrease in the polymerization degree and the increase in the total Ca^(2+)content of the slag,the surface tension of the slag increases with the increase in CaO/Al_(2)O_(3)mass ratio.The surface tension of the slag changes slightly with the temperature,irrespective of CaO/Al_(2)O_(3)mass ratio from 0.70 to 1.29 in the slag.