New insights in nano-copper chromite catalyzing ultrafine AP:Evaluation of dispersity and mixing uniformity

作     者：Yong Kou Peng Luo Lei Xiao Yanping Xin Guangpu Zhang Yubing Hu Junqing Yang Hongxu Gao Fengqi Zhao Wei Jiang Gazi Hao Yong Kou;Peng Luo;Lei Xiao;Yanping Xin;Guangpu Zhang;Yubing Hu;Junqing Yang;Hongxu Gao;Fengqi Zhao;Wei Jiang;Gazi Hao

作者机构：National Special Superfine Powder Engineering Research Center of ChinaSchool of Chemistry and Chemical EngineeringNanjing University of Science and TechnologyNanjing210094China Xi'an North Huian Chemical Industry Co.LtdXi'an710302China Xi'an Modern Chemistry Research InstituteXi'an710065China 

出 版 物：《Defence Technology（防务技术）》 (Defence Technology)

年 卷 期：2024年第32卷第2期

页      面：120-133页

核心收录：

学科分类：081702[工学-化学工艺] 07[理学] 08[工学] 0817[工学-化学工程与技术] 070205[理学-凝聚态物理] 080501[工学-材料物理与化学] 0805[工学-材料科学与工程（可授工学、理学学位）] 0702[理学-物理学] 

基　　金：the National Natural Science Foundation of China(Project Nos.21805139,21905023,12102194,22005144 and 22005145) the Joint Funds of the National Natural Science Foundation of China(Grant No.U2141202) Natural Science Foundation of Jiangsu Province(Grant No.BK20200471) the Fundamental Research Funds for the Central Universities(Grant Nos.30920041106,30921011203) Young Elite Scientists Sponsorship Program by CAST(Program,2021QNRC001) 

主　　题：Nano-CuCr_(2)O_(4) Ultrafine AP Dispersity UVeVis diffuse reflectance spectroscopy Thermal decomposition 

摘      要：Improving the application of nanomaterials has always been a research hotspot in the field of energetic materials(EMs)due to their obvious catalytic effect on the EMs,especially the uniformly dispersed ***,few studies have reported the dispersion of *** this study,the dispersity and mixing uniformity of nano-CuCr_(2)O_(4)was evaluated based on the difference of solid UV light absorption between the nano-catalytic materials and *** nano-CuCr_(2)O_(4)/ultrafine AP composites with different dispersity of nano-CuCr_(2)O_(4)were prepared by manual grinding and mechanical grinding with different grinding strength and griding *** then,the absorbance of different samples at 212 nm was obtained by solid UV testing due to the high repeatability of the absorbance at 210-214 nm for three parallel experiments,and the dispersity of different samples was calculated through the established difference ***,the samples were characterized by XRD,IR,SEM,EDS,DSC and TG-MS,which confirmed that different mixing methods did not change the structure of the samples(XRD and IR),and the mixing uniformity improved with the increase of grinding strength and grinding time(SEM and EDS).The scientificity and feasibility of the difference equation were further verified by *** dispersity of nano-CuCr_(2)O_(4)exhibits a positive intrinsic relationship with its catalytic performance,and the uniformly dispersed nano-CuCr_(2)O_(4)significantly reduces the thermal decomposition temperature of ultrafine AP from 367.7 to 338.8℃.The TG-MS patterns show that the dispersed nano-CuCr_(2)O_(4)advanced the thermal decomposition process of ultrafine AP by about 700 s,especially in the high temperature decomposition stage,and the more concentrated energy release characteristic is beneficial to further enhance the energy performance of AP-based *** above conclusions show that the evaluation method of dispersity based on solid UV curves could pro